| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.08 | g/cm3 |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.50to0.70 | % |
| MoldingShrinkage-AcrossFlow2 | | InternalMethod | 0.50to0.70 | % |
| 抗张强度3(屈服) | | ASTMD638 | 49.0 | MPa |
| 伸长率4(断裂) | | ASTMD638 | 35 | % |
| FlexuralModulus4(100mmSpan) | | ASTMD790 | 2280 | MPa |
| FlexuralStrength4(Yield,100mmSpan) | | ASTMD790 | 75.8 | MPa |
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 96 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 270 | J/m |
| 落锤冲击(23°C) | | ASTMD3029 | 13.6 | J |
| 载荷下热变形温度(1.8MPa,未退火,6.40mm) | | ASTMD648 | 113 | °C |
| RTIElec | | UL746 | 50.0 | °C |
| RTIImp | | UL746 | 50.0 | °C |
| RTIStr | | UL746 | 50.0 | °C |
| 耐电弧性5 | | ASTMD495 | PLC6 | |
| 相比耐漏电起痕指数(CTI) | | UL746 | PLC2 | |
| 高电弧燃烧指数(HAI) | | UL746 | PLC1 | |
| 高电压电弧起痕速率(HVTR) | | UL746 | PLC3 | |
| 热丝引燃(HWI) | | UL746 | PLC2 | |
| UL阻燃等级(1.5mm) | | UL94 | HB | |