性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.06 | g/cm3 |
MeltMass-FlowRate(MFR)(250°C/11.6kg) | | ASTMD1238 | 20to30 | g/10min |
收缩率-流动(3.18mm) | | ASTMD955 | 0.50to0.70 | % |
MoldingShrinkage-AcrossFlow(3.18mm) | | ASTMD955 | 0.50to0.70 | % |
抗张强度(屈服,3.17mm) | | ASTMD638 | 34.5 | MPa |
TensileStrength(Break,3.18mm) | | ASTMD638 | 34.5 | MPa |
伸长率(断裂,3.18mm) | | ASTMD638 | 70 | % |
弯曲模量(3.17mm) | | ASTMD790 | 1760 | MPa |
FlexuralStrength(Break,3.18mm) | | ASTMD790 | 48.3 | MPa |
悬壁梁缺口冲击强度 | -40°C,3.18mm | ASTMD256 | 190 | J/m |
悬壁梁缺口冲击强度 | -18°C,3.18mm | ASTMD256 | 270 | J/m |
悬壁梁缺口冲击强度 | 23°C,3.18mm | ASTMD256 | 370 | J/m |
落锤冲击(3.18mm) | | ASTMD3029 | 22.6 | J |
载荷下热变形温度(0.45MPa,未退火,3.18mm) | | ASTMD648 | 98.9 | °C |
载荷下热变形温度(1.8MPa,未退火,3.18mm) | | ASTMD648 | 93.3 | °C |
体积电阻率 | | ASTMD257 | 1.0E+16 | ohmscm |