| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.10 | g/cm3 |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.50to0.70 | % |
| MoldingShrinkage-AcrossFlow2 | | InternalMethod | 0.50to0.70 | % |
| 室外适用性 | | UL746C | f1 | |
| 抗张强度3(屈服) | | ASTMD638 | 57.9 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 46.9 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 6.5 | % |
| 伸长率4(断裂) | | ASTMD638 | 25 | % |
| FlexuralModulus4(100mmSpan) | | ASTMD790 | 2310 | MPa |
| FlexuralStrength4(Yield,100mmSpan) | | ASTMD790 | 82.7 | MPa |
| 悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 91 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 260 | J/m |
| 装有测量仪表的落镖冲击 | -30°C,EnergyatPeakLoad | ASTMD3763 | 16.3 | J |
| 装有测量仪表的落镖冲击 | 23°C,EnergyatPeakLoad | ASTMD3763 | 40.7 | J |
| 载荷下热变形温度(0.45MPa,未退火,6.40mm) | | ASTMD648 | 102 | °C |
| 载荷下热变形温度(1.8MPa,未退火,6.40mm) | | ASTMD648 | 92.8 | °C |
| RTIElec | | UL746 | 95.0 | °C |
| RTIImp | | UL746 | 80.0 | °C |
| RTIStr | | UL746 | 95.0 | °C |
| 表面电阻率 | | ASTMD257 | >1.0E+15 | ohms |
| 体积电阻率 | | ASTMD257 | 3.1E+16 | ohmscm |
| DielectricStrength(3.20mm,inOil) | | ASTMD149 | 18 | kV/mm |
| 介电常数 | 50Hz | ASTMD150 | 2.66 | |
| 介电常数 | 60Hz | ASTMD150 | 2.66 | |
| 介电常数 | 1MHz | ASTMD150 | 2.57 | |
| 耗散因数 | 50Hz | ASTMD150 | 6.0E-3 | |
| 耗散因数 | 60Hz | ASTMD150 | 6.0E-3 | |
| 耗散因数 | 1MHz | ASTMD150 | 2.6E-3 | |
| 耐电弧性5 | | ASTMD495 | PLC7 | |
| 相比耐漏电起痕指数(CTI) | | UL746 | PLC1 | |
| 高电压电弧起痕速率(HVTR) | | UL746 | PLC4 | |
| UL阻燃等级 | 1.5mm | UL94 | V-1 | |
| UL阻燃等级 | 6.0mm | UL94 | V-0 | |
| 极限氧指数 | | ASTMD2863 | 33 | % |
| RadiantPanelListing(UL) | | | YES | |