性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.08 | g/cm3 |
MeltMass-FlowRate(MFR)(300°C/3.8kg) | | ASTMD1238 | 20to40 | g/10min |
收缩率-流动(3.18mm) | | ASTMD955 | 0.90to1.2 | % |
抗张强度(屈服,3.17mm) | | ASTMD638 | 57.9 | MPa |
TensileStrength(Break,3.18mm) | | ASTMD638 | 55.2 | MPa |
弯曲模量(3.17mm) | | ASTMD790 | 2070 | MPa |
弯曲强度(3.18mm) | | ASTMD790 | 82.7 | MPa |
悬壁梁缺口冲击强度(23°C,3.18mm) | | ASTMD256 | 210 | J/m |
落锤冲击(3.18mm) | | ASTMD3029 | 28.2 | J |
载荷下热变形温度(0.45MPa,未退火,3.18mm) | | ASTMD648 | 141 | °C |
载荷下热变形温度(1.8MPa,未退火,3.18mm) | | ASTMD648 | 113 | °C |
UL阻燃等级 | 1.6mm | UL94 | HB | |
UL阻燃等级 | 3.2mm | UL94 | HB | |