| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.06 | g/cm3 |
| 密度 | | ISO1183 | 1.06 | g/cm3 |
| 熔流率（熔体流动速率）(280°C/5.0kg) | | ASTMD1238 | 8.0 | g/10min |
| 溶化体积流率（MVR）(280°C/5.0kg) | | ISO1133 | 8.00 | cm3/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.50to0.70 | % |
| 吸水率(饱和,23°C) | | ISO62 | 0.23 | % |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.060 | % |
| 拉伸模量2 | | ASTMD638 | 2400 | MPa |
| 拉伸模量 | | ISO527-2/1 | 2200 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 53.0 | MPa |
| 拉伸应力(屈服) | | ISO527-2/50 | 51.0 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 49.0 | MPa |
| 拉伸应力(断裂) | | ISO527-2/50 | 48.0 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 5.1 | % |
| 拉伸应变(屈服) | | ISO527-2/50 | 4.2 | % |
| 伸长率4(断裂) | | ASTMD638 | 40 | % |
| 拉伸应变(断裂) | | ISO527-2/50 | 40 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 2200 | MPa |
| 弯曲模量5 | | ISO178 | 2200 | MPa |
| FlexuralStress5,6 | | ISO178 | 77.0 | MPa |
| 弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 85.0 | MPa |
| 泰伯耐磨性(1000Cycles,1000g,CS-17转轮) | | InternalMethod | 75.0 | mg |
| 简支梁缺口冲击强度7 | -30°C | ISO179/1eA | 7.0 | kJ/m2 |
| 简支梁缺口冲击强度7 | 23°C | ISO179/1eA | 14 | kJ/m2 |
| 悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 110 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 160 | J/m |
| 悬壁梁缺口冲击强度8 | -30°C | ISO180/1A | 7.0 | kJ/m2 |
| 悬壁梁缺口冲击强度8 | 23°C | ISO180/1A | 11 | kJ/m2 |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 42.0 | J |
| 洛氏硬度(R级) | | ISO2039-2 | 116 | |
| 球压硬度(H358/30) | | ISO2039-1 | 95.0 | MPa |
| HeatDeflectionTemperature9(0.45MPa,Unannealed,64.0mmSpan) | | ISO75-2/Bf | 133 | °C |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 117 | °C |
| HeatDeflectionTemperature9(1.8MPa,Unannealed,64.0mmSpan) | | ISO75-2/Af | 117 | °C |
| 维卡软化温度 | | ASTMD152510 | 140 | °C |
| 维卡软化温度 | —— | ISO306/B50 | 139 | °C |
| 维卡软化温度 | —— | ISO306/B120 | 142 | °C |
| BallPressureTest(125°C) | | IEC60695-10-2 | Pass | |
| 线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 9.2E-5 | cm/cm/°C |
| 线形热膨胀系数-流动(-40到40°C) | | ISO11359-2 | 9.2E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 9.5E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ISO11359-2 | 9.5E-5 | cm/cm/°C |
| FlameRating(1.5mm,TestingbySABIC) | | UL94 | HB | |
| 灼热丝易燃指数(3.2mm) | | IEC60695-2-12 | 750 | °C |
| Gardner光泽度(60°,无织构) | | ASTMD523 | 20 | |