| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.11 | g/cm3 |
| 密度 | | ISO1183 | 1.12 | g/cm3 |
| 熔流率（熔体流动速率）(280°C/5.0kg) | | ASTMD1238 | 5.7 | g/10min |
| 溶化体积流率（MVR）(280°C/5.0kg) | | ISO1133 | 5.70 | cm3/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.50to0.80 | % |
| 吸水率(饱和,23°C) | | ISO62 | 0.20 | % |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.050 | % |
| 拉伸模量2 | | ASTMD638 | 2220 | MPa |
| 拉伸模量 | | ISO527-2/1 | 2440 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 64.0 | MPa |
| 拉伸应力(屈服) | | ISO527-2/50 | 64.0 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 53.0 | MPa |
| 拉伸应力(断裂) | | ISO527-2/50 | 58.0 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 4.6 | % |
| 拉伸应变(屈服) | | ISO527-2/50 | 4.7 | % |
| 伸长率4(断裂) | | ASTMD638 | 20 | % |
| 拉伸应变(断裂) | | ISO527-2/50 | 8.3 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 2390 | MPa |
| 弯曲模量5 | | ISO178 | 2360 | MPa |
| FlexuralStress5,6 | | ISO178 | 100 | MPa |
| 弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 100 | MPa |
| 简支梁缺口冲击强度7(23°C) | | ISO179/1eA | 20 | kJ/m2 |
| 悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 180 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 300 | J/m |
| 悬壁梁缺口冲击强度8 | -30°C | ISO180/1A | 15 | kJ/m2 |
| 悬壁梁缺口冲击强度8 | 23°C | ISO180/1A | 19 | kJ/m2 |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 52.0 | J |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 122 | °C |
| HeatDeflectionTemperature9(1.8MPa,Unannealed,64.0mmSpan) | | ISO75-2/Af | 124 | °C |
| 维卡软化温度 | | ASTMD152510 | 143 | °C |
| 维卡软化温度 | —— | ISO306/B50 | 143 | °C |
| 维卡软化温度 | —— | ISO306/B120 | 146 | °C |
| 线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 6.7E-5 | cm/cm/°C |
| 线形热膨胀系数-流动(-40到40°C) | | ISO11359-2 | 6.7E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 6.7E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ISO11359-2 | 6.7E-5 | cm/cm/°C |
| RTIElec | | UL746 | 65.0 | °C |
| RTIImp | | UL746 | 65.0 | °C |
| RTIStr | | UL746 | 65.0 | °C |
| 表面电阻率 | | ASTMD257 | 1.3E+18 | ohms |
| 表面电阻率 | | IEC60093 | 1.3E+18 | ohms |
| 体积电阻率 | | ASTMD257 | 7.6E+17 | ohmscm |
| 体积电阻率 | | IEC60093 | 7.6E+17 | ohmscm |
| DielectricStrength(3.20mm,inOil) | | ASTMD149 | 34 | kV/mm |
| 介电强度(3.20mm,在油中) | | IEC60243-1 | 34 | kV/mm |
| 介电常数(1MHz) | | ASTMD150 | 2.78 | |
| 相对电容率(1MHz) | | IEC60250 | 2.78 | |
| 耗散因数(1MHz) | | ASTMD150 | 2.9E-3 | |
| 耗散因数(1MHz) | | IEC60250 | 2.9E-3 | |
| 漏电起痕指数 | | IEC60112 | 225 | V |
| 高电弧燃烧指数(HAI) | | UL746 | PLC1 | |
| 热丝引燃(HWI) | | UL746 | PLC2 | |
| FlameRating(1.5mm,TestingbySABIC) | | UL94 | V-0 | |
| 灼热丝易燃指数(1.6mm) | | IEC60695-2-12 | 960 | °C |
| 热灯丝点火温度 | 1.0mm | IEC60695-2-13 | 775 | °C |
| 热灯丝点火温度 | 2.0mm | IEC60695-2-13 | 775 | °C |
| 热灯丝点火温度 | 3.0mm | IEC60695-2-13 | 800 | °C |
| 极限氧指数 | | ISO4589-2 | 34 | % |
| Ds_4min | | ISO5659-2 | 70 | |
| F1ClassSmokeandToxicityRating | | NFF16-101 | 3.00 | mm |