| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.20 | g/cm3 |
| 熔流率（熔体流动速率）(300°C/5.0kg) | | ASTMD1238 | 9.0 | g/10min |
| 溶化体积流率（MVR）(300°C/5.0kg) | | ISO1133 | 8.10 | cm3/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.20to0.50 | % |
| 吸水率(24hr) | | ASTMD570 | 0.060 | % |
| 室外适用性 | | UL746C | f1 | |
| 拉伸模量2 | | ASTMD638 | 6200 | MPa |
| 拉伸模量 | | ISO527-2/1 | 7070 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 90.0 | MPa |
| 拉伸应力(断裂) | | ISO527-2/5 | 97.3 | MPa |
| 伸长率4(断裂) | | ASTMD638 | 2.6 | % |
| 拉伸应变(断裂) | | ISO527-2/5 | 2.5 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 5800 | MPa |
| 弯曲模量5 | | ISO178 | 6540 | MPa |
| FlexuralStress5,6 | | ISO178 | 167 | MPa |
| 弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 160 | MPa |
| 简支梁缺口冲击强度(23°C) | | ISO179/2C | 12 | kJ/m2 |
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 96 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 120 | J/m |
| NotchedIzodImpactStrength7(23°C) | | ISO180/1A | 11 | kJ/m2 |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD4812 | 650 | J/m |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 22.6 | J |
| 洛氏硬度(L计秤) | | ASTMD785 | 106 | |
| 载荷下热变形温度 | 0.45MPa,未退火,3.20mm | ASTMD648 | 141 | °C |
| 载荷下热变形温度 | 0.45MPa,未退火,6.40mm | ASTMD648 | 143 | °C |
| HeatDeflectionTemperature8(0.45MPa,Unannealed,100mmSpan) | | ISO75-2/Be | 143 | °C |
| 载荷下热变形温度 | 1.8MPa,未退火,3.20mm | ASTMD648 | 135 | °C |
| 载荷下热变形温度 | 1.8MPa,未退火,6.40mm | ASTMD648 | 138 | °C |
| HeatDeflectionTemperature8(1.8MPa,Unannealed,100mmSpan) | | ISO75-2/Ae | 137 | °C |
| 维卡软化温度 | —— | ISO306/B50 | 143 | °C |
| 维卡软化温度 | —— | ISO306/B120 | 146 | °C |
| 线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 2.9E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 8.3E-5 | cm/cm/°C |
| RTIElec | | UL746 | 90.0 | °C |
| RTIImp | | UL746 | 90.0 | °C |
| RTIStr | | UL746 | 90.0 | °C |
| DielectricStrength(3.20mm,inOil) | | ASTMD149 | 17 | kV/mm |
| 介电常数 | 50Hz | ASTMD150 | 2.86 | |
| 介电常数 | 60Hz | ASTMD150 | 2.86 | |
| 耗散因数 | 50Hz | ASTMD150 | 8.0E-4 | |
| 耗散因数 | 60Hz | ASTMD150 | 8.0E-4 | |
| 耐电弧性9 | | ASTMD495 | PLC7 | |
| 高电弧燃烧指数(HAI) | | UL746 | PLC4 | |
| 高电压电弧起痕速率(HVTR) | | UL746 | PLC4 | |
| 热丝引燃(HWI) | | UL746 | PLC4 | |
| UL阻燃等级(1.5mm) | | UL94 | HB | |
| 极限氧指数 | | ASTMD2863 | 26 | % |