| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.06 | g/cm3 |
| 密度 | | ISO1183 | 1.06 | g/cm3 |
| 熔流率（熔体流动速率）(280°C/5.0kg) | | ASTMD1238 | 9.2 | g/10min |
| 溶化体积流率（MVR）(280°C/5.0kg) | | ISO1133 | 9.00 | cm3/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.50to0.70 | % |
| MoldingShrinkage-AcrossFlow(3.20mm) | | InternalMethod | 0.50to0.70 | % |
| 吸水率(24hr) | | ASTMD570 | 0.060 | % |
| 吸水率(饱和,23°C) | | ISO62 | 0.23 | % |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.060 | % |
| 拉伸模量2 | | ASTMD638 | 2860 | MPa |
| 拉伸模量 | | ISO527-2/1 | 2700 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 58.6 | MPa |
| 拉伸应力(屈服) | | ISO527-2/50 | 57.0 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 49.6 | MPa |
| 拉伸应力(断裂) | | ISO527-2/50 | 51.0 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 7.2 | % |
| 拉伸应变(屈服) | | ISO527-2/50 | 3.5 | % |
| 伸长率4(断裂) | | ASTMD638 | 28 | % |
| 拉伸应变(断裂) | | ISO527-2/50 | 17 | % |
| 弯曲模量 | 50.0mm跨距4 | ASTMD790 | 2650 | MPa |
| 弯曲模量 | 100mmSpan5 | ASTMD790 | 2420 | MPa |
| 弯曲模量6 | | ISO178 | 2550 | MPa |
| FlexuralStress6,7 | | ISO178 | 95.0 | MPa |
| 弯曲强度 | 屈服,50.0mm跨距4 | ASTMD790 | 90.3 | MPa |
| 弯曲强度 | Yield,100mmSpan5 | ASTMD790 | 89.6 | MPa |
| CharpyNotchedImpactStrength8(23°C) | | ISO179/1eA | 17 | kJ/m2 |
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 130 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 210 | J/m |
| 悬壁梁缺口冲击强度9 | -30°C | ISO180/1A | 5.0 | kJ/m2 |
| 悬壁梁缺口冲击强度9 | 23°C | ISO180/1A | 17 | kJ/m2 |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 48.8 | J |
| 落锤冲击 | -40°C | ASTMD3029 | 5.42 | J |
| 落锤冲击 | -30°C | ASTMD3029 | 25.8 | J |
| 洛氏硬度(R级) | | ASTMD785 | 119 | |
| 载荷下热变形温度 | 0.45MPa,未退火,3.20mm | ASTMD648 | 132 | °C |
| 载荷下热变形温度 | 0.45MPa,未退火,6.40mm | ASTMD648 | 137 | °C |
| 载荷下热变形温度 | 1.8MPa,未退火,3.20mm | ASTMD648 | 118 | °C |
| 载荷下热变形温度 | 1.8MPa,未退火,6.40mm | ASTMD648 | 127 | °C |
| HeatDeflectionTemperature10(1.8MPa,Unannealed,64.0mmSpan) | | ISO75-2/Af | 120 | °C |
| 维卡软化温度 | | ASTMD152511 | 149 | °C |
| 维卡软化温度 | —— | ISO306/B50 | 140 | °C |
| 维卡软化温度 | —— | ISO306/B120 | 143 | °C |
| 线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 9.2E-5 | cm/cm/°C |
| 线形热膨胀系数-流动(-40到40°C) | | ISO11359-2 | 9.2E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 9.5E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ISO11359-2 | 9.5E-5 | cm/cm/°C |
| RTIElec | | UL746 | 105 | °C |
| RTIImp | | UL746 | 90.0 | °C |
| RTIStr | | UL746 | 105 | °C |
| DielectricStrength(3.20mm,inOil) | | ASTMD149 | 22 | kV/mm |
| 介电常数 | 50Hz | ASTMD150 | 2.65 | |
| 介电常数 | 60Hz | ASTMD150 | 2.65 | |
| 耗散因数 | 50Hz | ASTMD150 | 4.0E-4 | |
| 耗散因数 | 60Hz | ASTMD150 | 4.0E-4 | |
| 耐电弧性12 | | ASTMD495 | PLC7 | |
| 相比耐漏电起痕指数(CTI) | | UL746 | PLC3 | |
| 高电弧燃烧指数(HAI) | | UL746 | PLC0 | |
| 高电压电弧起痕速率(HVTR) | | UL746 | PLC4 | |
| 热丝引燃(HWI) | | UL746 | PLC2 | |
| UL阻燃等级(1.5mm) | | UL94 | HB | |