| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.24 | g/cm3 |
| 密度 | | ISO1183 | 1.24 | g/cm3 |
| 熔流率（熔体流动速率）(300°C/5.0kg) | | ASTMD1238 | 18 | g/10min |
| 溶化体积流率（MVR）(280°C/5.0kg) | | ISO1133 | 15.0 | cm3/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.50to0.70 | % |
| 吸水率(饱和,23°C) | | ISO62 | 0.23 | % |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.070 | % |
| 拉伸模量2 | | ASTMD638 | 3600 | MPa |
| 拉伸模量 | | ISO527-2/1 | 3790 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 69.0 | MPa |
| 拉伸应力(屈服) | | ISO527-2/5 | 76.0 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 66.6 | MPa |
| 拉伸应力(断裂) | | ISO527-2/5 | 75.0 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 3.2 | % |
| 拉伸应变(屈服) | | ISO527-2/5 | 3.4 | % |
| 伸长率4(断裂) | | ASTMD638 | 4.5 | % |
| 拉伸应变(断裂) | | ISO527-2/5 | 3.6 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 3570 | MPa |
| 弯曲模量5 | | ISO178 | 3620 | MPa |
| FlexuralStress5,6 | | ISO178 | 127 | MPa |
| 弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 120 | MPa |
| 简支梁缺口冲击强度7(23°C) | | ISO179/1eA | 26 | kJ/m2 |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 45 | J/m |
| NotchedIzodImpactStrength8(23°C) | | ISO180/1A | 7.0 | kJ/m2 |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 10.6 | J |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 140 | °C |
| HeatDeflectionTemperature9(1.8MPa,Unannealed,64.0mmSpan) | | ISO75-2/Af | 140 | °C |
| 维卡软化温度 | | ASTMD152510 | 149 | °C |
| 维卡软化温度 | | ISO306/B120 | 155 | °C |
| 线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 4.4E-5 | cm/cm/°C |
| 线形热膨胀系数-流动(-40到40°C) | | ISO11359-2 | 4.4E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 7.1E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ISO11359-2 | 7.1E-5 | cm/cm/°C |
| 表面电阻率 | | IEC60093 | 3.0E+13to5.0E+13 | ohms |
| 体积电阻率 | | IEC60093 | 14to16 | ohmscm |
| 介电强度(3.20mm,在油中) | | IEC60243-1 | 27 | kV/mm |
| 相对电容率(1MHz) | | IEC60250 | 2.97 | |
| 漏电起痕指数 | | IEC60112 | 400 | V |
| 高电弧燃烧指数(HAI) | | UL746 | PLC4 | |
| 热丝引燃(HWI) | | UL746 | PLC0 | |
| UL阻燃等级 | 1.0mm,TestingbySABIC | UL94 | V-1 | |
| UL阻燃等级 | 3.0mm,TestingbySABIC | UL94 | V-0 | |
| 灼热丝易燃指数(1.0mm) | | IEC60695-2-12 | 960 | °C |
| 热灯丝点火温度 | 1.0mm | IEC60695-2-13 | 775 | °C |
| 热灯丝点火温度 | 2.0mm | IEC60695-2-13 | 775 | °C |
| 热灯丝点火温度 | 2.5mm | IEC60695-2-13 | 775 | °C |
| 热灯丝点火温度 | 3.0mm | IEC60695-2-13 | 775 | °C |