性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.05 | g/cm3 |
MeltMass-FlowRate(MFR)(250°C/11.6kg) | | ASTMD1238 | 12to18 | g/10min |
收缩率-流动(3.18mm) | | ASTMD955 | 0.50to0.70 | % |
抗张强度(屈服,3.17mm) | | ASTMD638 | 46.9 | MPa |
TensileStrength(Break,3.18mm) | | ASTMD638 | 43.4 | MPa |
伸长率(屈服,3.18mm) | | ASTMD638 | 3.0 | % |
伸长率(断裂,3.18mm) | | ASTMD638 | 25 | % |
弯曲模量(3.17mm) | | ASTMD790 | 2210 | MPa |
弯曲强度(3.18mm) | | ASTMD790 | 72.4 | MPa |
简支梁缺口冲击强度(23°C) | | ISO179/1 | 15 | kJ/m2 |
悬壁梁缺口冲击强度 | -40°C,3.18mm | ASTMD256 | 130 | J/m |
悬壁梁缺口冲击强度 | 23°C,3.18mm | ASTMD256 | 210 | J/m |
悬壁梁缺口冲击强度 | -30°C | ISO180/1A | 4.2 | kJ/m2 |
悬壁梁缺口冲击强度 | 23°C | ISO180/1A | 15 | kJ/m2 |
落锤冲击(3.18mm) | | ASTMD3029 | 16.9 | J |
洛氏硬度(R级) | | ASTMD785 | 114 | |
载荷下热变形温度(0.45MPa,未退火,3.18mm) | | ASTMD648 | 113 | °C |
载荷下热变形温度(1.8MPa,未退火,3.18mm) | | ASTMD648 | 107 | °C |
维卡软化温度 | | ASTMD15252 | 127 | °C |
体积电阻率 | | ASTMD257 | 1.0E+16 | ohmscm |