| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.69 | g/cm3 |
| 密度 | | ISO1183 | 1.69 | g/cm3 |
| 熔流率（熔体流动速率）(337°C/6.6kg) | | ASTMD1238 | 20 | g/10min |
| 溶化体积流率（MVR）(360°C/5.0kg) | | ISO1133 | 20.0 | cm3/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.20to0.30 | % |
| MoldingShrinkage-AcrossFlow(3.20mm) | | InternalMethod | 0.30to0.50 | % |
| 吸水率(饱和,23°C) | | ISO62 | 0.10 | % |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.040 | % |
| 拉伸模量2 | | ASTMD638 | 14900 | MPa |
| 拉伸模量 | | ISO527-2/1 | 14700 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 125 | MPa |
| 拉伸应力(屈服) | | ISO527-2/5 | 121 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 125 | MPa |
| 拉伸应力(断裂) | | ISO527-2/5 | 121 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 2.5 | % |
| 拉伸应变(屈服) | | ISO527-2/5 | 1.4 | % |
| 伸长率4(断裂) | | ASTMD638 | 2.5 | % |
| 拉伸应变(断裂) | | ISO527-2/5 | 1.4 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 12900 | MPa |
| 弯曲模量5 | | ISO178 | 13600 | MPa |
| FlexuralStress5,6 | | ISO178 | 172 | MPa |
| 弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 180 | MPa |
| 简支梁缺口冲击强度7(23°C) | | ISO179/1eA | 4.8 | kJ/m2 |
| 悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 50 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 50 | J/m |
| 悬壁梁缺口冲击强度8 | -30°C | ISO180/1A | 5.4 | kJ/m2 |
| 悬壁梁缺口冲击强度8 | 23°C | ISO180/1A | 5.6 | kJ/m2 |
| UnnotchedIzodImpactStrength8(23°C) | | ISO180/1U | 5.6 | kJ/m2 |
| ReverseNotchIzodImpact(3.20mm) | | ASTMD256 | 110 | J/m |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 12.0 | J |
| HeatDeflectionTemperature9(0.45MPa,Unannealed,64.0mmSpan) | | ISO75-2/Bf | 195 | °C |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 183 | °C |
| HeatDeflectionTemperature9(1.8MPa,Unannealed,64.0mmSpan) | | ISO75-2/Af | 182 | °C |
| 维卡软化温度 | | ASTMD152510 | 184 | °C |
| 维卡软化温度 | —— | ISO306/B50 | 187 | °C |
| 维卡软化温度 | —— | ISO306/B120 | 195 | °C |
| BallPressureTest(125°C) | | IEC60695-10-2 | Pass | |
| CLTE-Flow(-40to150°C) | | ASTME831 | 1.6E-5 | cm/cm/°C |
| 线形热膨胀系数-流动(23到150°C) | | ISO11359-2 | 1.6E-5 | cm/cm/°C |
| CLTE-Transverse(-40to150°C) | | ASTME831 | 3.8E-5 | cm/cm/°C |
| CLTE-Transverse(23to150°C) | | ISO11359-2 | 3.8E-5 | cm/cm/°C |
| 表面电阻率 | | ASTMD257 | 2.1E+15 | ohms |
| 体积电阻率 | | ASTMD257 | 6.0E+15 | ohmscm |