| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.26 | g/cm3 |
| 密度 | | ISO1183 | 1.27 | g/cm3 |
| 熔流率（熔体流动速率）(337°C/6.6kg) | | ASTMD1238 | 24 | g/10min |
| MeltVolume-FlowRate(MVR)(340°C/5.0kg) | | ISO1133 | 16.0 | cm3/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.50to0.70 | % |
| MoldingShrinkage-AcrossFlow2 | | InternalMethod | 0.50to0.70 | % |
| 吸水率(饱和,23°C) | | ISO62 | 0.90 | % |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.50 | % |
| 拉伸模量 | | ISO527-2/1 | 3000 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 96.5 | MPa |
| 伸长率4(断裂) | | ASTMD638 | 70 | % |
| FlexuralModulus4(100mmSpan) | | ASTMD790 | 3170 | MPa |
| 弯曲模量5 | | ISO178 | 3100 | MPa |
| FlexuralStrength4(Yield,100mmSpan) | | ASTMD790 | 145 | MPa |
| 简支梁缺口冲击强度6 | -30°C | ISO179/1eA | 4.0 | kJ/m2 |
| 简支梁缺口冲击强度6 | 23°C | ISO179/1eA | 4.0 | kJ/m2 |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 53 | J/m |
| 悬壁梁缺口冲击强度7 | -30°C | ISO180/1A | 5.0 | kJ/m2 |
| 悬壁梁缺口冲击强度7 | 23°C | ISO180/1A | 5.0 | kJ/m2 |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD4812 | 2100 | J/m |
| ReverseNotchIzodImpact(3.20mm) | | ASTMD256 | 2100 | J/m |
| HeatDeflectionTemperature8(0.45MPa,Unannealed,100mmSpan) | | ISO75-2/Be | 195 | °C |
| 载荷下热变形温度(1.8MPa,未退火,6.40mm) | | ASTMD648 | 190 | °C |
| HeatDeflectionTemperature8(1.8MPa,Unannealed,100mmSpan) | | ISO75-2/Ae | 180 | °C |
| 维卡软化温度 | | ISO306/B120 | 205 | °C |
| 线形热膨胀系数-流动(23到150°C) | | ISO11359-2 | 6.0E-5 | cm/cm/°C |
| CLTE-Transverse(23to150°C) | | ISO11359-2 | 6.0E-5 | cm/cm/°C |
| 导热系数 | | ISO8302 | 0.23 | W/m/K |
| 补充信息 | | TestMethod | NominalValue | Unit |
| MetallizedHazeOnset | | InternalMethod | 195 | °C |