| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.12 | g/cm3 |
| 密度 | | ISO1183 | 1.12 | g/cm3 |
| TensileModulus(1.91mm,CompressionMolded) | | ASTMD638 | 3.00 | MPa |
| TensileModulus(1.91mm,CompressionMolded) | | ISO527-2 | 3.00 | MPa |
| TensileStrength(Yield,1.91mm,CompressionMolded) | | ASTMD638 | 7.24 | MPa |
| TensileStress(Yield,1.91mm,CompressionMolded) | | ISO527-2 | 7.24 | MPa |
| TensileElongation(Break,1.91mm,CompressionMolded) | | ASTMD638 | 380 | % |
| TensileStrain(Break,1.91mm,CompressionMolded) | | ISO527-2 | 380 | % |
| 弹性体 | | TestMethod | NominalValue | Unit |
| 拉伸永久变形 | | ASTMD412 | 12 | % |
| TearStrength2(24°C) | | ASTMD624 | 26.3 | kN/m |
| 压缩永久变形 | 24°C,22hr | ASTMD395B | 27 | % |
| 压缩永久变形 | 100°C,22hr | ASTMD395B | 69 | % |
| 压缩永久变形 | 24°C,22hr | ISO815 | 27 | % |
| 压缩永久变形 | 100°C,22hr | ISO815 | 69 | % |
| DurometerHardness(ShoreA,1.91mm,CompressionMolded) | | ASTMD2240 | 60 | |
| IRHD硬度 | | ISO48 | 60 | |
| ChangeinShoreHardnessinAir(125°C,168hr) | | ISO188 | 61 | |
| ChangeinUltimateElongation(125°C,168hr) | | ASTMD471 | 380 | % |
| ChangeinDurometerHardness(125°C,168hr) | | ASTMD471 | 61 | |
| 体积变化 | 24°C,168hr,inReferenceFuelB | ASTMD471 | 8.0 | % |
| 体积变化 | 100°C,168hr,inASTM#1Oil | ASTMD471 | -30 | % |
| 体积变化 | 100°C,168hr,inASTM#3Oil | ASTMD471 | -6.0 | % |
| 体积变化 | 100°C,168hr,在水中 | ASTMD471 | 9.0 | % |