性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | | 1.50 | g/cm3 |
SpiralFlow2 | | ASTMD3123 | 3.10 | cm |
收缩率-流动2 | | | 0.30 | % |
MoldingShrinkage-AcrossFlow2 | | | 1.0 | % |
吸水率(平衡) | | ASTMD570 | 0.040 | % |
拉伸模量(23°C) | | ASTMD638 | 11500 | MPa |
抗张强度(屈服,23°C) | | ASTMD638 | 185 | MPa |
伸长率(断裂,23°C) | | ASTMD638 | 2.0to3.0 | % |
弯曲模量(23°C) | | ASTMD790 | 10500 | MPa |
弯曲强度(23°C) | | ASTMD790 | 280 | MPa |
悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 60 | J/m |
悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 610 | J/m |
DurometerHardness(ShoreD,23°C) | | ASTMD2240 | 92 | |
载荷下热变形温度(1.8MPa,未退火) | | ASTMD648 | 358 | °C |
连续使用温度 | | UL746B | 280 | °C |
玻璃转化温度 | | ASTMD3418 | 152 | °C |
熔融温度 | | ASTMD3418 | 372 | °C |
表面电阻率 | | ASTMD257 | 1.0E+16 | ohms |
体积电阻率 | | ASTMD257 | 1.0E+16 | ohmscm |
DielectricStrength(3.20mm) | | ASTMD149 | 20 | kV/mm |
ArcResistance3 | | ASTMD495 | 160 | sec |
ComparativeTrackingIndex4 | | ASTMD3638 | 140 | V |
UL阻燃等级(0.8mm) | | UL94 | V-0 | |