性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.06 | g/cm3 |
收缩率-流动(3.20mm) | | InternalMethod | 0.50to0.70 | % |
吸水率(24hr) | | ASTMD570 | 0.10 | % |
抗张强度2(屈服) | | ASTMD638 | 62.1 | MPa |
伸长率2(断裂) | | ASTMD638 | 30 | % |
FlexuralModulus3(100mmSpan) | | ASTMD790 | 2280 | MPa |
FlexuralStrength3(Yield,100mmSpan) | | ASTMD790 | 100 | MPa |
悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 160 | J/m |
悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 290 | J/m |
载荷下热变形温度(0.45MPa,未退火,6.40mm) | | ASTMD648 | 154 | °C |
载荷下热变形温度(1.8MPa,未退火,6.40mm) | | ASTMD648 | 146 | °C |
线形热膨胀系数-流动(0到100°C) | | ASTME831 | 7.2E-5 | cm/cm/°C |
RTIElec | | UL746 | 50.0 | °C |
RTIImp | | UL746 | 50.0 | °C |
RTIStr | | UL746 | 50.0 | °C |
UL阻燃等级(0.70mm) | | UL94 | HB | |