| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.08 | g/cm3 |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.50to0.70 | % |
| 吸水率(24hr) | | ASTMD570 | 0.070 | % |
| 室外适用性 | | UL746C | f1 | |
| 抗张强度2(屈服) | | ASTMD638 | 63.4 | MPa |
| 伸长率2(断裂) | | ASTMD638 | 25 | % |
| FlexuralModulus3(100mmSpan) | | ASTMD790 | 2550 | MPa |
| FlexuralStrength3(Yield,100mmSpan) | | ASTMD790 | 99.3 | MPa |
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 130 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 190 | J/m |
| 落锤冲击 | -40°C | ASTMD3029 | 4.07 | J |
| 落锤冲击 | -30°C | ASTMD3029 | 14.9 | J |
| 洛氏硬度(R级) | | ASTMD785 | 119 | |
| 载荷下热变形温度(1.8MPa,未退火,6.40mm) | | ASTMD648 | 123 | °C |
| 线形热膨胀系数-流动(-40到95°C) | | ASTME831 | 5.9E-5 | cm/cm/°C |
| RTIElec | | UL746 | 110 | °C |
| RTIImp | | UL746 | 105 | °C |
| RTIStr | | UL746 | 110 | °C |
| DielectricStrength(3.20mm,inOil) | | ASTMD149 | 20 | kV/mm |
| 介电常数 | 50Hz | ASTMD150 | 2.69 | |
| 介电常数 | 60Hz | ASTMD150 | 2.69 | |
| 耗散因数 | 50Hz | ASTMD150 | 7.0E-4 | |
| 耗散因数 | 60Hz | ASTMD150 | 7.0E-4 | |
| 耐电弧性4 | | ASTMD495 | PLC6 | |
| 相比耐漏电起痕指数(CTI) | | UL746 | PLC1 | |
| 高电压电弧起痕速率(HVTR) | | UL746 | PLC4 | |
| UL阻燃等级 | 1.5mm | UL94 | V-1 | |
| UL阻燃等级 | 6.0mm | UL94 | V-0 | |
| 极限氧指数 | | ASTMD2863 | 29 | % |
| RadiantPanelListing(UL) | | | RP100 | |