性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.10 | g/cm3 |
MeltMass-FlowRate(MFR)(300°C/3.8kg) | | ASTMD1238 | 10to30 | g/10min |
收缩率-流动(3.18mm) | | ASTMD955 | 1.0to1.3 | % |
MoldingShrinkage-AcrossFlow(3.18mm) | | ASTMD955 | 0.90to1.2 | % |
抗张强度(屈服,3.17mm) | | ASTMD638 | 57.9 | MPa |
TensileStrength(Break,3.18mm) | | ASTMD638 | 55.2 | MPa |
伸长率(断裂,3.18mm) | | ASTMD638 | 50 | % |
弯曲模量(3.17mm) | | ASTMD790 | 2210 | MPa |
弯曲强度(3.18mm) | | ASTMD790 | 93.1 | MPa |
悬壁梁缺口冲击强度 | -30°C,3.18mm | ASTMD256 | 110 | J/m |
悬壁梁缺口冲击强度 | 23°C,3.18mm | ASTMD256 | 190 | J/m |
落锤冲击(3.18mm) | | ASTMD3029 | 28.2 | J |
洛氏硬度(R级) | | ASTMD785 | 116 | |
载荷下热变形温度(0.45MPa,未退火,3.18mm) | | ASTMD648 | 154 | °C |
载荷下热变形温度(1.8MPa,未退火,3.18mm) | | ASTMD648 | 129 | °C |
维卡软化温度 | | ASTMD15252 | 199 | °C |