| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.20 | g/cm3 |
| 特定体积 | | ASTMD792 | 0.830 | cm3/g |
| 密度 | | ASTMD792 | 1.19 | g/cm3 |
| 密度 | | ISO1183 | 1.20 | g/cm3 |
| 熔流率（熔体流动速率）(300°C/1.2kg) | | ASTMD1238 | 3.0 | g/10min |
| 溶化体积流率（MVR）(300°C/1.2kg) | | ISO1133 | 3.00 | cm3/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.70to0.80 | % |
| 吸水率(24hr) | | ASTMD570 | 0.16 | % |
| 吸水率(饱和,23°C) | | ISO62 | 0.16 | % |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.35 | % |
| 拉伸模量2 | | ASTMD638 | 2090 | MPa |
| 拉伸模量 | | ISO527-2/1 | 2260 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 65.5 | MPa |
| 拉伸应力 | 屈服 | ISO527-2/5 | 65.0 | MPa |
| 拉伸应力 | 屈服 | ISO527-2/50 | 65.0 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 71.7 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 7.0 | % |
| 拉伸应变(屈服) | | ISO527-2/50 | 7.0 | % |
| 伸长率4(断裂) | | ASTMD638 | 120 | % |
| 拉伸应变(断裂) | | ISO527-2/50 | >50 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 2030 | MPa |
| 弯曲模量5 | | ISO178 | 2120 | MPa |
| FlexuralStress5,6 | | ISO178 | 66.0 | MPa |
| 弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 95.1 | MPa |
| 简支梁缺口冲击强度7(23°C) | | ISO179/1eA | 15 | kJ/m2 |
| 悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 140 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 640 | J/m |
| 悬壁梁缺口冲击强度8 | -30°C | ISO180/1A | 11 | kJ/m2 |
| 悬壁梁缺口冲击强度8 | 23°C | ISO180/1A | 13 | kJ/m2 |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD4812 | 3200 | J/m |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 73.0 | J |
| 落锤冲击(23°C) | | ASTMD3029 | 149 | J |
| 拉伸冲击强度9 | | ASTMD1822 | 578 | kJ/m2 |
| 洛氏硬度 | M计秤 | ASTMD785 | 85 | |
| 洛氏硬度 | R计秤 | ASTMD785 | 122 | |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 143 | °C |
| HeatDeflectionTemperature10(1.8MPa,Unannealed,64.0mmSpan) | | ISO75-2/Af | 132 | °C |
| 维卡软化温度 | | ASTMD152511 | 160 | °C |
| 维卡软化温度 | —— | ISO306/B50 | 154 | °C |
| 维卡软化温度 | —— | ISO306/B120 | 155 | °C |
| 线形热膨胀系数-流动 | -40to40°C | ASTME831 | 6.0E-5 | cm/cm/°C |
| 线形热膨胀系数-流动 | -40到95°C | ASTME831 | 9.2E-5 | cm/cm/°C |
| 线形热膨胀系数-流动(-40到40°C) | | ISO11359-2 | 6.0E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 6.0E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ISO11359-2 | 6.0E-5 | cm/cm/°C |
| 比热 | | ASTMC351 | 1260 | J/kg/°C |
| 导热系数 | | ASTMC177 | 0.21 | W/m/K |
| RTIElec | | UL746 | 125 | °C |
| RTIImp | | UL746 | 125 | °C |
| RTIStr | | UL746 | 125 | °C |
| 体积电阻率 | | ASTMD257 | >2.6E+17 | ohmscm |
| 介电强度(3.20mm,inAir) | | ASTMD149 | 20 | kV/mm |
| 介电常数 | 50Hz | ASTMD150 | 3.15 | |
| 介电常数 | 60Hz | ASTMD150 | 3.15 | |
| 介电常数 | 1MHz | ASTMD150 | 3.00 | |
| 耗散因数 | 50Hz | ASTMD150 | 1.2E-3 | |
| 耗散因数 | 60Hz | ASTMD150 | 1.2E-3 | |
| 耗散因数 | 100Hz | ASTMD150 | 0.024 | |
| 相比耐漏电起痕指数(CTI) | | UL746 | PLC3 | |
| 高电弧燃烧指数(HAI) | | UL746 | PLC4 | |
| 高电压电弧起痕速率(HVTR) | | UL746 | PLC3 | |