| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.20 | g/cm3 |
| 密度 | | ISO1183 | 1.20 | g/cm3 |
| MeltMass-FlowRate(MFR)(330°C/2.16kg) | | ASTMD1238 | 15 | g/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.970.97 | % |
| MoldingShrinkage-AcrossFlow(3.20mm) | | InternalMethod | 0.970.97 | % |
| 拉伸模量2 | | ASTMD638 | 2170 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 68.0 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 70.0 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 7.5 | % |
| 伸长率4(断裂) | | ASTMD638 | 120 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 2210 | MPa |
| 弯曲强度5(断裂,50.0mm跨距) | | ASTMD790 | 105 | MPa |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 580 | J/m |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD4812 | 2100 | J/m |
| 装有测量仪表的落镖冲击 | 23°C,EnergyatPeakLoad | ASTMD3763 | 73.0 | J |
| 装有测量仪表的落镖冲击 | 23°C,TotalEnergy | ASTMD3763 | 77.0 | J |
| 载荷下热变形温度(0.45MPa,未退火,3.20mm) | | ASTMD648 | 160 | °C |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 147 | °C |
| 维卡软化温度 | | ASTMD15255 | 164 | °C |
| BallPressureTest(125°C) | | IEC60695-10-2 | Pass | |