| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.34 | g/cm3 |
| 熔流率（熔体流动速率）(337°C/6.6kg) | | ASTMD1238 | 7.8 | g/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.50to0.60 | % |
| 吸水率(24hr) | | ASTMD570 | 0.21 | % |
| 吸水率(平衡,23°C) | | ASTMD570 | 1.2 | % |
| 拉伸模量2 | | ASTMD638 | 4690 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 114 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 116 | MPa |
| 伸长率4(断裂) | | ASTMD638 | 6.0 | % |
| FlexuralModulus4(100mmSpan) | | ASTMD790 | 5170 | MPa |
| FlexuralStrength4(Break,100mmSpan) | | ASTMD790 | 200 | MPa |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 85 | J/m |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD4812 | 480 | J/m |
| ReverseNotchIzodImpact(3.20mm) | | ASTMD256 | 510 | J/m |
| 洛氏硬度(M级) | | ASTMD785 | 114 | |
| 载荷下热变形温度(0.45MPa,未退火,6.40mm) | | ASTMD648 | 210 | °C |
| 载荷下热变形温度(1.8MPa,未退火,6.40mm) | | ASTMD648 | 209 | °C |
| 维卡软化温度 | | ASTMD15255 | 223 | °C |
| CLTE-Flow(-20to150°C) | | ASTME831 | 3.2E-5 | cm/cm/°C |
| RTIElec | | UL746 | 170 | °C |
| RTIImp | | UL746 | 170 | °C |
| RTIStr | | UL746 | 170 | °C |
| 体积电阻率 | | ASTMD257 | 1.0E+17 | ohmscm |
| DielectricStrength(1.60mm,inOil) | | ASTMD149 | 28 | kV/mm |
| 介电常数(1kHz) | | ASTMD150 | 3.50 | |
| 耗散因数 | 1kHz | ASTMD150 | 1.4E-3 | |
| 耗散因数 | 2.45GHz | ASTMD150 | 4.6E-3 | |
| 耐电弧性6 | | ASTMD495 | PLC6 | |
| 相比耐漏电起痕指数(CTI) | | UL746 | PLC4 | |
| 高电弧燃烧指数(HAI) | | UL746 | PLC4 | |
| 高电压电弧起痕速率(HVTR) | | UL746 | PLC2 | |
| 热丝引燃(HWI) | | UL746 | PLC1 | |
| UL阻燃等级 | 0.41mm | UL94 | V-0 | |
| UL阻燃等级 | 1.9mm | UL94 | 5VA | |
| 极限氧指数 | | ASTMD2863 | 47 | % |
| NBSSmokeDensity-Flaming,Ds,4min | | ASTME662 | 1.80 | |