| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.34 | g/cm3 |
| Thickness-LayerCapability | | | 254.0到330.2 | um |
| 拉伸模量3(3.18mm) | | ASTMD638 | 2220 | MPa |
| 抗张强度3(3.18mm) | | ASTMD638 | 71.7 | MPa |
| 伸长率3(断裂,3.18mm) | | ASTMD638 | 6.0 | % |
| 弯曲模量4 | | ASTMD790 | 2500 | MPa |
| 弯曲强度4 | | ASTMD790 | 115 | MPa |
| 压缩模量 | | ASTMD732 | 1930 | MPa |
| 压缩强度 | | ASTMD695 | 105 | MPa |
| 剪切强度(6.35mm) | | ASTMD732 | 57.2 | MPa |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256A | 110 | J/m |
| 无缺口悬臂梁冲击(23°C) | | ASTMD256 | 610 | J/m |
| 载荷下热变形温度(1.8MPa,未退火,3.18mm) | | ASTMD648 | 153 | °C |
| 玻璃转化温度 | | DSC | 367 | °C |
| 线形热膨胀系数-流动 | | ASTME228 | 6.6E-5 | cm/cm/°C |
| 介电强度5,6 | | ASTMD149 | 4.3到11 | kV/mm |
| 介电常数6 | | ASTMD150 | 3.00到3.20 | |
| 耗散因数6 | | ASTMD150 | 2.6E-3到2.7E-3 | |
| VolumeResistance6 | | ASTMD257 | 6.0E+13到1.0E+14 | ohms |
| UL阻燃等级 | | UL94 | V-0 | |
| NBSSmokeDensity | flaming | ASTMF814/E662 | Passed | |
| NBSSmokeDensity | non-flaming | ASTMF814/E662 | Passed | |
| OSU总放热量 | 2mintest | FAR25.853 | 16.0 | kWmin/m2 |
| OSU总放热量 | 5mintest | FAR25.853 | 36.0 | kW/m2 |
| 垂直燃烧-60秒(1.02到6.35mm) | | FAR25.853 | 2.0 | sec |
| 放热-65/65,<40HRPeak(1.52mm) | | FAR25.853 | Passed | |
| 可燃性-FAA | | FAR25.853 | <5.00 | |
| UL阻燃等级 | | UL94 | V-0 | |
| NBSSmokeDensity | flaming | ASTMF814/E662 | Passed | |
| NBSSmokeDensity | non-flaming | ASTMF814/E662 | Passed | |
| OSU总放热量 | 2mintest | FAR25.853 | 16.0 | kWmin/m2 |
| OSU总放热量 | 5mintest | FAR25.853 | 36.0 | kW/m2 |
| 垂直燃烧-60秒(1.02到6.35mm) | | FAR25.853 | 2.0 | sec |
| 放热-65/65,<40HRPeak(1.52mm) | | FAR25.853 | Passed | |
| 可燃性-FAA | | FAR25.853 | <5.00 | |
| Outgassing | CollectedVolatileCondensableMaterial(CVCM) | ASTME595 | -0.10 | % |
| Outgassing | TotalMassLost(TML) | ASTME595 | 0.41 | % |
| Outgassing | WaterVaporRecovered(WVR) | ASTME595 | -0.37 | % |
| 抗真菌性-Method508.6 | | MILSTD-810G | Passed | |