| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 0.988 | g/cm3 |
| 熔流率（熔体流动速率）(260°C/5.0kg) | | ASTMD1238 | 14 | g/10min |
| 溶化体积流率（MVR）(260°C/5.0kg) | | ISO1133 | 12.0 | cm3/10min |
| 收缩率-流动(3.20mm) | | InternalMethod | 0.60to0.70 | % |
| MoldingShrinkage-AcrossFlow(3.20mm) | | InternalMethod | 0.60to0.80 | % |
| 拉伸模量2 | | ASTMD638 | 1240 | MPa |
| 拉伸模量 | | ISO527-2/1 | 1380 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 35.9 | MPa |
| 拉伸应力(屈服) | | ISO527-2/50 | 35.0 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 34.5 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 8.0 | % |
| 伸长率4(断裂) | | ASTMD638 | 130 | % |
| 拉伸应变(断裂) | | ISO527-2/50 | 75 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 1380 | MPa |
| 弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 51.7 | MPa |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 530 | J/m |
| 装有测量仪表的落镖冲击 | -30°C,TotalEnergy | ASTMD3763 | 30.0 | J |
| 装有测量仪表的落镖冲击 | 23°C,TotalEnergy | ASTMD3763 | 37.0 | J |
| 载荷下热变形温度(0.45MPa,未退火,3.20mm) | | ASTMD648 | 113 | °C |
| HeatDeflectionTemperature5(0.45MPa,Unannealed,64.0mmSpan) | | ISO75-2/Bf | 116 | °C |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 85.0 | °C |
| 维卡软化温度 | | ASTMD15256 | 86.7 | °C |
| 维卡软化温度 | | ISO306/A50 | 131 | °C |
| 线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 1.6E-4 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 9.7E-5 | cm/cm/°C |