性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.37 | g/cm3 |
熔流率(熔体流动速率) | 280°C/5.0kg | ASTMD1238 | 19 | g/10min |
熔流率(熔体流动速率) | 300°C/5.0kg | ASTMD1238 | 46 | g/10min |
抗张强度2(屈服,3.20mm) | | ASTMD638 | 108 | MPa |
TensileStrength2(Break,3.20mm) | | ASTMD638 | 108 | MPa |
TensileElongation2(Yield,3.20mm) | | ASTMD638 | 6.0 | % |
伸长率2(断裂,3.20mm) | | ASTMD638 | 6.0 | % |
弯曲模量3(3.20mm) | | ASTMD790 | 8730 | MPa |
弯曲强度3(断裂,3.20mm) | | ASTMD790 | 157 | MPa |
悬壁梁缺口冲击强度(23°C,3.20mm) | | ASTMD256 | 69 | J/m |
无缺口悬臂梁冲击(23°C,3.20mm) | | ASTMD256 | 350 | J/m |
载荷下热变形温度(1.8MPa,未退火,6.40mm) | | ASTMD648 | 121 | °C |
UL阻燃等级 | 1.6mm | UL94 | V-1 | |
UL阻燃等级 | 3.2mm | UL94 | V-0 | |