| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 密度 | | ASTMD1505 | 0.935 | g/cm3 |
| 熔流率（熔体流动速率）(190°C/2.16kg) | | ASTMD1238 | 0.50 | g/10min |
| 醋酸乙烯含量 | | | 13.5 | wt% |
| 抗张强度(断裂,模压成型) | | ASTMD638 | 25.0 | MPa |
| 伸长率(断裂,模压成型) | | ASTMD638 | 680 | % |
| SecantModulus-2%Secant,MD(50um,BlownFilm) | | ASTMD882 | 60.0 | MPa |
| SecantModulus-2%Secant,TD(50um,BlownFilm) | | ASTMD882 | 70.0 | MPa |
| TensileStrength-MD(Break,50um,BlownFilm) | | ASTMD882 | 32.0 | MPa |
| TensileStrength-TD(Break,50um,BlownFilm) | | ASTMD882 | 32.0 | MPa |
| TensileElongation-MD(Break,50um,BlownFilm) | | ASTMD882 | 750 | % |
| TensileElongation-TD(Break,50um,BlownFilm) | | ASTMD882 | 800 | % |
| 落锤冲击(50um,吹塑薄膜) | | ASTMD1709B | 730 | g |
| ElmendorfTearStrength-MD(50um,BlownFilm) | | ASTMD1922 | 240 | g |
| ElmendorfTearStrength-TD(50um,BlownFilm) | | ASTMD1922 | 350 | g |
| 肖氏硬度 | 邵氏A,模压成型 | ASTMD2240 | 91 | |
| 肖氏硬度 | 邵氏D,模压成型 | ASTMD2240 | 50 | |
| 维卡软化温度 | | ASTMD15252 | 75.0 | °C |
| 熔融峰值温度 | | ASTMD3418 | 94.0 | °C |
| 光泽度(45°,50.0um,吹塑薄膜) | | ASTMD2457 | 95 | |
| 雾度(50.0um,吹塑薄膜) | | ASTMD1003 | 2.0 | % |