性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.940 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 20 | g/10min |
醋酸乙烯含量 | | | 20.0 | wt% |
TensileStrength-MD2(Break) | | ASTMD882A | 15.0 | MPa |
TensileStrength-TD2(Break) | | ASTMD882A | 13.0 | MPa |
TensileElongation-MD2(Break) | | ASTMD882A | 520 | % |
TensileElongation-TD2(Break) | | ASTMD882A | 610 | % |
维卡软化温度 | | ASTMD1525 | 51.0 | °C |
熔融峰值温度 | | ASTMD3418 | 83.0 | °C |