性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.925 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 2.0 | g/10min |
醋酸乙烯含量 | | | 2.5 | wt% |
薄膜厚度-经测试 | | | 32 | um |
SecantModulus-1%Secant,MD2(32um,BlownFilm) | | ASTMD882 | 138 | MPa |
SecantModulus-1%Secant,TD2(32um,BlownFilm) | | ASTMD882 | 152 | MPa |
TensileStrength-MD2(Break,32um,BlownFilm) | | ASTMD882 | 24.0 | MPa |
TensileStrength-TD2(Break,32um,BlownFilm) | | ASTMD882 | 17.0 | MPa |
TensileElongation-MD2(Break,32um,BlownFilm) | | ASTMD882 | 350 | % |
TensileElongation-TD2(Break,32um,BlownFilm) | | ASTMD882 | 700 | % |
DartDropImpact2(32um,BlownFilm) | | ASTMD1709A | 150 | g |
光泽度(45°,31.8um,吹塑薄膜) | | ASTMD2457 | 79 | |
雾度(31.8um,吹塑薄膜) | | ASTMD1003 | 3.3 | % |