性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD4883 | 0.906 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 0.50 | g/10min |
薄膜厚度-经测试 | | | 25 | um |
SecantModulus-1%Secant,MD2(25um,BlownFilm) | | ASTMD882 | 124 | MPa |
SecantModulus-1%Secant,TD2(25um,BlownFilm) | | ASTMD882 | 145 | MPa |
TensileStrength-TD2(Yield,25um,BlownFilm) | | ASTMD882 | 8.00 | MPa |
TensileStrength-MD2(Break,25um,BlownFilm) | | ASTMD882 | 62.0 | MPa |
TensileStrength-TD2(Break,25um,BlownFilm) | | ASTMD882 | 45.0 | MPa |
TensileElongation-MD2(Break,25um,BlownFilm) | | ASTMD882 | 600 | % |
TensileElongation-TD2(Break,25um,BlownFilm) | | ASTMD882 | 1000 | % |
落锤冲击2(25um,吹塑薄膜) | | ASTMD1709 | >2000 | g |
ElmendorfTearStrength-MD2(25um,BlownFilm) | | ASTMD1922 | 600 | g |
ElmendorfTearStrength-TD2(25um,BlownFilm) | | ASTMD1922 | 650 | g |
始封温度3(25um,吹塑薄膜) | | InternalMethod | 82.0 | °C |
光泽度(45°,25.4um,吹塑薄膜) | | ASTMD2457 | 60 | |
雾度(25.4um,吹塑薄膜) | | ASTMD1003 | 8.0 | % |