性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD4883 | 0.910 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 2.0 | g/10min |
薄膜厚度-经测试 | | | 25 | um |
SecantModulus-1%Secant,MD2(25um,BlownFilm) | | ASTMD882 | 152 | MPa |
SecantModulus-1%Secant,TD2(25um,BlownFilm) | | ASTMD882 | 172 | MPa |
TensileStrength-MD2(Break,25um,BlownFilm) | | ASTMD882 | 35.0 | MPa |
TensileStrength-TD2(Break,25um,BlownFilm) | | ASTMD882 | 40.0 | MPa |
TensileElongation-MD2(Break,25um,BlownFilm) | | ASTMD882 | 700 | % |
TensileElongation-TD2(Break,25um,BlownFilm) | | ASTMD882 | 1200 | % |
落锤冲击2(25um,吹塑薄膜) | | ASTMD1709A | 400 | g |
ElmendorfTearStrength-MD2(25um,BlownFilm) | | ASTMD1922 | 300 | g |
ElmendorfTearStrength-TD2(25um,BlownFilm) | | ASTMD1922 | 550 | g |
始封温度3(25um,吹塑薄膜) | | InternalMethod | 88.0 | °C |
光泽度(45°,25.4um,吹塑薄膜) | | ASTMD2457 | 55 | |
雾度(25.4um,吹塑薄膜) | | ASTMD1003 | 13 | % |