性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.900 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 3.0 | g/10min |
抗张强度 | AcrossFlow:Break,1.20mm,ExtrudedSheet | ASTMD638 | 33.8 | MPa |
抗张强度 | Flow:Break,1.20mm,ExtrudedSheet | ASTMD638 | 30.9 | MPa |
伸长率 | AcrossFlow:Break,1.20mm,ExtrudedSheet | ASTMD638 | 840 | % |
伸长率 | Flow:Break,1.20mm,ExtrudedSheet | ASTMD638 | 750 | % |
FlexuralModulus(1.20mm,ExtrudedSheet) | | ASTMD790 | 73.5 | MPa |
弹性体 | | TestMethod | NominalValue | Unit |
撕裂强度 | AcrossFlow:1.20mm | ASTMD1004 | 68.6 | kN/m |
撕裂强度 | Flow:1.20mm | ASTMD1004 | 70.6 | kN/m |
DurometerHardness(ShoreA,1.20mm,ExtrudedSheet) | | ASTMD2240 | 86 | |
维卡软化温度 | | ASTMD1525 | 82.0 | °C |
熔融峰值温度 | | ASTMD3418 | 91.0 | °C |