| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 门尼粘度 | 121°C2 | ASTMD1646 | 8 | MU |
| 门尼粘度 | 121°C | ASTMD1646 | 12 | MU |
| 门尼粘度 | ML1+4,100°C3 | ASTMD1646 | 11 | MU |
| 门尼粘度 | ML1+4,100°C2 | ASTMD1646 | 23 | MU |
| 门尼粘度 | ML1+4,100°C | ASTMD1646 | 37 | MU |
| 肖氏硬度 | 邵氏A2 | ASTMD2240 | 63 | |
| 肖氏硬度 | 邵氏A | ASTMD2240 | 60 | |
| 拉伸应力2(100%应变) | | ASTMD412 | 3.10 | MPa |
| 抗张强度 | 屈服2 | ASTMD412 | 11.0 | MPa |
| 抗张强度 | 屈服 | ASTMD412 | 14.3 | MPa |
| 伸长率2(断裂) | | ASTMD412 | 360 | % |
| 撕裂强度4 | ——2 | ASTMD624 | 27.7 | kN/m |
| 撕裂强度4 | —— | ASTMD624 | 28.2 | kN/m |
| 压缩永久变形 | 150°C,70hr2 | ASTMD395 | 25 | % |
| 压缩永久变形 | 150°C,70hr | ASTMD395 | 22 | % |
| 压缩永久变形 | 150°C,138hr | ASTMD395 | 31 | % |
| 压缩永久变形 | 150°C,168hr2 | ASTMD395 | 35 | % |
| ChangeinGlassTransitionTemperature | ——5 | ASTMD471 | -46 | °C |
| ChangeinGlassTransitionTemperature | ——6 | ASTMD471 | -52 | °C |
| ChangeinGlassTransitionTemperature | ——7 | ASTMD471 | -44 | °C |
| ChangeinGlassTransitionTemperature | ——8 | ASTMD471 | -51 | °C |
| ChangeinGlassTransitionTemperature | 150°C9 | ASTMD573 | -47 | °C |
| ChangeinGlassTransitionTemperature | 150°C10 | ASTMD573 | -42 | °C |
| ChangeinGlassTransitionTemperature | 175°C11 | ASTMD573 | -43 | °C |
| ChangeinGlassTransitionTemperature | 175°C12 | ASTMD573 | -41 | °C |
| 玻璃转化温度 | ——2 | ASTMD3418 | -54.0 | °C |
| 玻璃转化温度 | —— | ASTMD3418 | -42.0 | °C |
| 玻璃转化温度 | DMAResults-dandelta13 | ASTMD3418 | -41 | °C |
| 玻璃转化温度 | DMAResults-dandelta14 | ASTMD3418 | -32 | °C |
| 玻璃转化温度 | DMAResults-lossmodulus13 | ASTMD3418 | -45 | °C |
| 玻璃转化温度 | DMAResults-lossmodulus14 | ASTMD3418 | -37 | °C |
| 玻璃转化温度 | StaticO-Ringtest13 | ASTMD3418 | -63 | °C |
| 玻璃转化温度 | StaticO-Ringtest14 | ASTMD3418 | -55 | °C |
| 玻璃转化温度 | TR10 | ASTMD3418 | -39 | °C |
| 玻璃转化温度 | TR102 | ASTMD3418 | -45 | °C |
| 玻璃转化温度 | TR302 | ASTMD3418 | -33 | °C |
| 玻璃转化温度 | TR30 | ASTMD3418 | -32 | °C |
| MDR | MH:177°C15 | ASTMD5289 | 9.63 | dNm |
| MDR | MH:177°C16 | ASTMD5289 | 7.83 | dNm |
| MDR | ML:177°C15 | ASTMD5289 | 0.410 | dNm |
| MDR | ML:177°C16 | ASTMD5289 | 0.370 | dNm |
| MDR | t50:177°C15 | ASTMD5289 | 2.1 | min |
| MDR | t50:177°C16 | ASTMD5289 | 2.1 | min |
| MDR | t90:177°C15 | ASTMD5289 | 9.4 | min |
| MDR | t90:177°C16 | ASTMD5289 | 8.9 | min |
| MDR | ts2:177°C16 | ASTMD5289 | 1.4 | min |
| MDR | ts2:177°C15 | ASTMD5289 | 1.2 | min |
| MooneyScorch | t10:121°C | ASTMD1646 | 14.8 | min |
| MooneyScorch | t10:121°C2 | ASTMD1646 | 17.4 | min |
| MooneyScorch | t32 | ASTMD1646 | 10.1 | min |
| MooneyScorch | t3:121°C | ASTMD1646 | 9.2 | min |
| 挥发性 | | 内部方法 | 0.6 | wt% |