性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 0.880 | g/cm3 |
密度 | | ISO1183 | 0.880 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 3.7 | g/10min |
熔流率(熔体流动速率)(190°C/2.16kg) | | ISO1133 | 3.7 | g/10min |
抗张强度 | Break,20°C2 | ASTMD638 | 14.4 | MPa |
抗张强度 | 断裂,23°C3 | ASTMD638 | 6.43 | MPa |
拉伸应力4 | Break,20°C | ISO527-2/50 | 14.4 | MPa |
拉伸应力4 | 断裂,23°C | ISO527-2/500 | 6.43 | MPa |
伸长率 | 断裂,23°C2 | ASTMD638 | 590 | % |
伸长率 | 断裂,23°C3 | ASTMD638 | 550 | % |
TensileStrain4 | 断裂,23°C | ISO527-2/50 | 590 | % |
TensileStrain4 | 断裂,23°C | ISO527-2/500 | 550 | % |
FlexuralModulus5(23°C) | | ASTMD790 | 22.5 | MPa |
肖氏硬度(邵氏D) | | ASTMD2240 | 30 | |
肖氏硬度(邵氏D) | | ISO868 | 30 | |
玻璃转化温度 | | ASTMD3418 | -48.0 | °C |
维卡软化温度 | | ASTMD1525 | 42.0 | °C |
维卡软化温度 | | ISO306 | 42.0 | °C |
熔融峰值温度 | | ASTMD3418 | 53.9 | °C |
溶融温度(DSC) | | ISO3146 | 54.0 | °C |
结晶峰温度(DSC)12 | | ASTMD3418 | 35.0 | °C |
补充信息 | | TestMethod | NominalValue | Unit |
MaximumProcessingTemperature | | | 290 | °C |