| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.06 | g/cm3 |
| MeltMass-FlowRate(MFR)(250°C/11.6kg) | | ASTMD1238 | 4.0to9.0 | g/10min |
| 收缩率-流动(3.18mm) | | ASTMD955 | 0.50to0.70 | % |
| MoldingShrinkage-AcrossFlow(3.18mm) | | ASTMD955 | 0.50to0.70 | % |
| 抗张强度(屈服,3.17mm) | | ASTMD638 | 64.1 | MPa |
| TensileStrength(Break,3.18mm) | | ASTMD638 | 62.1 | MPa |
| 伸长率(屈服,3.18mm) | | ASTMD638 | 5.0 | % |
| 伸长率(断裂,3.18mm) | | ASTMD638 | 25 | % |
| 弯曲模量(3.17mm) | | ASTMD790 | 2410 | MPa |
| 弯曲强度(3.18mm) | | ASTMD790 | 89.6 | MPa |
| 简支梁缺口冲击强度(23°C) | | ISO179/1 | 15 | kJ/m2 |
| 悬壁梁缺口冲击强度 | -30°C,3.18mm | ASTMD256 | 110 | J/m |
| 悬壁梁缺口冲击强度 | 23°C,3.18mm | ASTMD256 | 210 | J/m |
| 悬壁梁缺口冲击强度(23°C) | | ISO180/1A | 15 | kJ/m2 |
| 落锤冲击(3.18mm) | | ASTMD3029 | 16.9 | J |
| 载荷下热变形温度(0.45MPa,未退火,3.18mm) | | ASTMD648 | 129 | °C |
| 载荷下热变形温度(1.8MPa,未退火,3.18mm) | | ASTMD648 | 121 | °C |
| 维卡软化温度 | | ASTMD15252 | 135 | °C |
| RTIElec | 0.75mm | UL746 | 65.0 | °C |
| RTIElec | 1.5mm | UL746 | 110 | °C |
| RTIElec | 1.7mm | UL746 | 110 | °C |
| RTIElec | 3.0mm | UL746 | 110 | °C |
| RTIImp | 0.75mm | UL746 | 65.0 | °C |
| RTIImp | 1.5mm | UL746 | 105 | °C |
| RTIImp | 1.7mm | UL746 | 105 | °C |
| RTIImp | 3.0mm | UL746 | 105 | °C |
| RTIStr | 0.75mm | UL746 | 65.0 | °C |
| RTIStr | 1.5mm | UL746 | 110 | °C |
| RTIStr | 1.7mm | UL746 | 110 | °C |
| RTIStr | 3.0mm | UL746 | 110 | °C |
| 体积电阻率 | | ASTMD257 | 1.0E+17 | ohmscm |
| 介电强度(3.00mm) | | ASTMD149 | 24 | kV/mm |
| ComparativeTrackingIndex(CTI)(0.750mm) | | UL746 | PLC2 | |
| 高电弧燃烧指数(HAI) | 1.5mm | UL746 | PLC1 | |
| 高电弧燃烧指数(HAI) | 1.7mm | UL746 | PLC1 | |
| 高电弧燃烧指数(HAI) | 3.0mm | UL746 | PLC1 | |
| HighVoltageArcTrackingRate(HVTR)(0.750mm) | | UL746 | PLC3 | |
| 热丝引燃(HWI) | 1.5mm | UL746 | PLC0 | |
| 热丝引燃(HWI) | 1.7mm | UL746 | PLC0 | |
| 热丝引燃(HWI) | 3.0mm | UL746 | PLC0 | |
| UL阻燃等级 | 0.75mm,BK | UL94 | V-2 | |
| UL阻燃等级 | 1.5mm,ALL | UL94 | V-1 | |
| UL阻燃等级 | 1.7mm,ALL | UL94 | V-1 | |
| UL阻燃等级 | 3.0mm,ALL | UL94 | V-1 | |