| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.11 | g/cm3 |
| 熔流率（熔体流动速率）(230°C/5.0kg) | | ASTMD1238 | 6.0 | g/10min |
| 溶化体积流率（MVR） | 260°C/5.0kg | ISO1133 | 22.0 | cm3/10min |
| 溶化体积流率（MVR） | 280°C/5.0kg | ISO1133 | 47.0 | cm3/10min |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.070 | % |
| 拉伸模量2 | | ASTMD638 | 2670 | MPa |
| 拉伸模量 | | ISO527-2/1 | 2580 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 57.0 | MPa |
| 拉伸应力(屈服) | | ISO527-2/50 | 53.0 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 43.0 | MPa |
| 拉伸应力(断裂) | | ISO527-2/50 | 42.0 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 3.0 | % |
| 拉伸应变(屈服) | | ISO527-2/50 | 2.7 | % |
| 伸长率4(断裂) | | ASTMD638 | 15 | % |
| 拉伸应变(断裂) | | ISO527-2/50 | 27 | % |
| 弯曲模量 | 50.0mm跨距4 | ASTMD790 | 2700 | MPa |
| 弯曲模量 | 6.40mm | ASTMD790 | 2700 | MPa |
| 弯曲模量5 | | ISO178 | 2390 | MPa |
| FlexuralStress5,6 | | ISO178 | 83.0 | MPa |
| 弯曲强度 | 屈服,50.0mm跨距4 | ASTMD790 | 86.0 | MPa |
| 弯曲强度 | Yield,6.40mm | ASTMD790 | 88.0 | MPa |
| 简支梁缺口冲击强度7(23°C) | | ISO179/1eA | 10 | kJ/m2 |
| CharpyUnnotchedImpactStrength7(-30°C) | | ISO179/1eU | 6.0 | kJ/m2 |
| 悬壁梁缺口冲击强度 | -30°C | ASTMD256 | 100 | J/m |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 250 | J/m |
| 悬壁梁缺口冲击强度8 | -30°C | ISO180/1A | 7.0 | kJ/m2 |
| 悬壁梁缺口冲击强度8 | 23°C | ISO180/1A | 10 | kJ/m2 |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 30.0 | J |
| 载荷下热变形温度 | 0.45MPa,未退火,3.20mm | ASTMD648 | 88.0 | °C |
| 载荷下热变形温度 | 0.45MPa,未退火,6.40mm | ASTMD648 | 92.0 | °C |
| HeatDeflectionTemperature9(0.45MPa,Unannealed,64.0mmSpan) | | ISO75-2/Bf | 90.0 | °C |
| 载荷下热变形温度 | 1.8MPa,未退火,3.20mm | ASTMD648 | 78.0 | °C |
| 载荷下热变形温度 | 1.8MPa,未退火,6.40mm | ASTMD648 | 82.0 | °C |
| HeatDeflectionTemperature9(1.8MPa,Unannealed,64.0mmSpan) | | ISO75-2/Af | 79.0 | °C |
| 维卡软化温度 | | ASTMD152510 | 98.0 | °C |
| RTIElec | | UL746 | 65.0 | °C |
| RTIImp | | UL746 | 65.0 | °C |
| RTIStr | | UL746 | 65.0 | °C |
| 体积电阻率 | | IEC60093 | 1.0E+16 | ohmscm |
| 漏电起痕指数 | | IEC60112 | 250 | V |
| 高电弧燃烧指数(HAI) | | UL746 | PLC3 | |
| 热丝引燃(HWI) | | UL746 | PLC2 | |
| FlameRating(1.5mm,TestingbySABIC) | | UL94 | V-0 | |
| 充模分析 | | TestMethod | NominalValue | Unit |
| 熔体粘度(280°C,1500sec^-1) | | ISO11443 | 98.0 | Pas |