性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 0.934 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 0.80 | g/10min |
薄膜厚度-经测试 | | | 25 | um |
SecantModulus-1%Secant,MD(25um,BlownFilm) | | ASTMD882 | 370 | MPa |
SecantModulus-1%Secant,TD(25um,BlownFilm) | | ASTMD882 | 440 | MPa |
TensileStrength-MD(Yield,25um,BlownFilm) | | ASTMD882 | 16.0 | MPa |
TensileStrength-TD(Yield,25um,BlownFilm) | | ASTMD882 | 18.0 | MPa |
TensileStrength-MD(Break,25um,BlownFilm) | | ASTMD882 | 46.0 | MPa |
TensileStrength-TD(Break,25um,BlownFilm) | | ASTMD882 | 32.0 | MPa |
TensileElongation-MD(Break,25um,BlownFilm) | | ASTMD882 | 580 | % |
TensileElongation-TD(Break,25um,BlownFilm) | | ASTMD882 | 780 | % |
落锤冲击(25um,吹塑薄膜) | | ASTMD1709A | 80 | g |
ElmendorfTearStrength-MD(25um,BlownFilm) | | ASTMD1922 | 80 | g |
ElmendorfTearStrength-TD(25um,BlownFilm) | | ASTMD1922 | 570 | g |
光泽度(45°,25.0um,吹塑薄膜) | | ASTMD2457 | 63 | |
雾度(25.0um,吹塑薄膜) | | ASTMD1003 | 9.0 | % |
补充信息 | | TestMethod | NominalValue | Unit |
LowFrictionPuncture-BlownFilm(25.0um) | | InternalMethod | 270 | J/cm |