性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 0.934 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 5.0 | g/10min |
抗环境应力开裂(100%Igepal,模压成型,F50) | | ASTMD1693B | 1000 | hr |
抗张强度(屈服,模压成型) | | ASTMD638 | 17.9 | MPa |
伸长率(断裂,模压成型) | | ASTMD638 | 400 | % |
FlexuralModulus-Tangent(CompressionMolded) | | ASTMD790 | 862 | MPa |
载荷下热变形温度(0.45MPa,未退火,模压成型) | | ASTMD648 | 64.0 | °C |
载荷下热变形温度(1.8MPa,未退火,模压成型) | | ASTMD648 | 41.0 | °C |
UL阻燃等级 | 1.5mm | UL94 | HB | |
UL阻燃等级 | 3.0mm | UL94 | HB | |