性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.28 | g/cm3 |
熔流率(熔体流动速率)(280°C/5.0kg) | | ASTMD1238 | 9.0 | g/10min |
收缩率-流动(3.20mm) | | InternalMethod | 0.10to0.30 | % |
MoldingShrinkage-AcrossFlow(3.20mm) | | InternalMethod | 0.50to0.70 | % |
抗张强度2(屈服,3.20mm) | | ASTMD638 | 127 | MPa |
伸长率2(断裂,3.20mm) | | ASTMD638 | 3.0 | % |
弯曲模量3(3.20mm) | | ASTMD790 | 6960 | MPa |
弯曲强度3(断裂,3.20mm) | | ASTMD790 | 177 | MPa |
悬壁梁缺口冲击强度(23°C,3.20mm) | | ASTMD256 | 140 | J/m |
载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 135 | °C |
维卡软化温度 | | ASTMD15254 | 148 | °C |
CLTE-Flow(-30to130°C) | | ASTMD696 | 1.7E-5 | cm/cm/°C |
CLTE-Transverse(-30to130°C) | | ASTMD696 | 7.0E-5 | cm/cm/°C |
RTIElec | | UL746 | 65.0 | °C |
RTIImp | | UL746 | 65.0 | °C |
RTIStr | | UL746 | 65.0 | °C |
体积电阻率(23°C) | | ASTMD257 | 1.0E+11 | ohmscm |
介电强度(23°C) | | ASTMD149 | 36 | kV/mm |
漏电起痕指数 | | IEC60112 | 4.00 | V |
UL阻燃等级 | 0.8mm | UL94 | HB | |
UL阻燃等级 | 1.5mm | UL94 | HB | |
UL阻燃等级 | 3.0mm | UL94 | HB | |