性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
密度 | | ASTMD1505 | 0.935 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 0.60 | g/10min |
抗环境应力开裂(模压成型,F50) | | ASTMD1693B | >10000 | hr |
抗张强度(断裂,模压成型) | | ASTMD638 | 39.2 | MPa |
伸长率(断裂,模压成型) | | ASTMD638 | 850 | % |
弯曲模量(模压成型) | | ASTMD790 | 588 | MPa |
NotchedIzodImpact(-30°C,CompressionMolded) | | ASTMD256 | 98 | J/m |
维卡软化温度 | | ASTMD1525 | 122 | °C |
熔融峰值温度 | | ASTMD3418 | 125 | °C |
Gloss(45°,CompressionMolded) | | ASTMD2457 | 75 | |