| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 密度 | | BS2782620A | 1.51 | g/cm3 |
| 熔流率（熔体流动速率）(190°C/2.16kg) | | 内部方法 | 7.5 | g/10min |
| 拉伸应力 | | IEC60811-1-1 | 14.0 | MPa |
| 拉伸应变(断裂) | | IEC60811-1-1 | 150 | % |
| 拉伸强度的变化率 | 70°C,72hr,在ASTM#2油中 | | -47 | % |
| 拉伸强度的变化率 | 100°C,24hr,在ASTM#2油中 | | -58 | % |
| 拉伸强度的变化率 | 135°C,168hr | IEC60811-1-2 | 20 | % |
| 断裂时拉伸应力变化 | 70°C,72hr,在ASTM#2油中 | | 3.0 | % |
| 断裂时拉伸应力变化 | 100°C,24hr,在ASTM#2油中 | | -20 | % |
| 断裂时拉伸应力变化 | 135°C,168hr | IEC60811-1-2 | -15 | % |
| 冷弯曲(-30°C) | | IEC60811-1-4 | pass | |
| 热固性2 | Elongationunderload,20N/cm2:200°C | IEC60811-2-1 | 30 | % |
| 热固性2 | Permanentelongationaftercooling | IEC60811-2-1 | 0.0 | % |
| 温度指数 | | ISO4589-3 | >300 | °C |
| InsulationConstant-Ki | 20°C | IEC60502 | 1.3E+12 | ohmscm |
| InsulationConstant-Ki | 90°C | IEC60502 | 2.9E+8 | ohmscm |
| 传导率-ofgases | | IEC60754-2 | 13.0 | uS/cm |
| 极限氧指数 | | ISO4589-2 | 36 | % |
| 烟气中的腐蚀性气体-pH | | IEC60754-2 | 4.60 | |
| 烟雾密度 | | ASTMD2843 | <3.5 | % |
| HalogenAcidGasEvolution | | IEC60754-1 | <0.50 | % |
| PressureTest-K=1(100°C) | | IEC60811-2-1 | 40 | % |