| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 密度 | | | 1.30 | g/cm3 |
| SpiralFlow2 | | ASTMD3123 | 40.8 | cm |
| 收缩率-流动3 | | | 1.0 | % |
| MoldingShrinkage-AcrossFlow3 | | | 1.3 | % |
| 吸水率(平衡) | | ASTMD570 | 0.070 | % |
| 拉伸模量(23°C) | | ASTMD638 | 4200 | MPa |
| 抗张强度(屈服,23°C) | | ASTMD638 | 110 | MPa |
| 伸长率(断裂,23°C) | | ASTMD638 | 10to15 | % |
| 弯曲模量(23°C) | | ASTMD790 | 4100 | MPa |
| 弯曲强度(23°C) | | ASTMD790 | 185 | MPa |
| 压缩强度(23°C) | | ASTMD695 | 135 | MPa |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 60 | J/m |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | NoBreak | |
| 洛氏硬度(M计秤,23°C) | | ASTMD785 | 98 | |
| DurometerHardness(ShoreD,23°C) | | ASTMD2240 | 87 | |
| 载荷下热变形温度(1.8MPa,未退火) | | ASTMD648 | 175 | °C |
| 连续使用温度 | | UL746B | 280 | °C |
| 玻璃转化温度 | | ASTMD3418 | 152 | °C |
| 熔融温度 | | ASTMD3418 | 372 | °C |
| 表面电阻率 | | ASTMD257 | 1.0E+16 | ohms |
| 体积电阻率 | | ASTMD257 | 1.0E+16 | ohmscm |
| DielectricStrength(3.20mm) | | ASTMD149 | 17 | kV/mm |
| 耐电弧性4 | | ASTMD495 | 175 | sec |
| ComparativeTrackingIndex5 | | ASTMD3638 | 145 | V |
| UL阻燃等级(0.8mm) | | UL94 | V-0 | |
| 充模分析 | | TestMethod | NominalValue | Unit |
| MeltViscosity(400°C,1000sec^-1) | | ASTMD3835 | 250to300 | Pas |