| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | | 0.970 | g/cm3 |
| 门尼粘度(ML1+4,100°C) | | ASTMD1646 | 65 | MU |
| AcrylonitrileContent-Bound | | 内部方法 | 28.0 | % |
| Stabilizer | | | Non-staining | |
| 可溶性-inMEK | | | 100 | % |
| 肖氏硬度 | 邵氏A2 | ASTMD2240 | 72 | |
| 肖氏硬度 | 邵氏A3 | ASTMD2240 | 73 | |
| 拉伸应力 | 300%应变4 | ASTMD412 | 9.71 | MPa |
| 拉伸应力 | 300%应变5 | ASTMD412 | 10.5 | MPa |
| 拉伸应力 | 300%应变6 | ASTMD412 | 11.0 | MPa |
| 抗张强度 | 屈服2 | ASTMD412 | 28.6 | MPa |
| 抗张强度 | 屈服3 | ASTMD412 | 27.8 | MPa |
| 抗张强度 | 屈服7 | ASTMD412 | 28.2 | MPa |
| 伸长率 | 断裂4 | ASTMD412 | 610 | % |
| 伸长率 | 断裂5 | ASTMD412 | 580 | % |
| 伸长率 | 断裂6 | ASTMD412 | 560 | % |
| 撕裂强度8,3 | | ASTMD624 | 59.8 | kN/m |
| 压缩永久变形7(100°C,70hr) | | ASTMD395 | 60 | % |
| 空气中拉伸强度的变化率3(100°C,70hr) | | ASTMD865 | -6.0 | % |
| 空气中极限伸长率的变化率3(100°C,70hr) | | ASTMD865 | -24 | % |
| 空气中硬度计硬度的变化率3(邵氏A,100°C,70hr) | | ASTMD865 | 2.0 | |
| 拉伸强度的变化率3 | 100°C,70hr,在ASTM#1油中 | ASTMD471 | -7.0 | % |
| 拉伸强度的变化率3 | 100°C,70hr,在ASTM#3油中 | ASTMD471 | -26 | % |
| 极限伸长率的变化率3 | 100°C,70hr,在ASTM#1油中 | ASTMD471 | -19 | % |
| 极限伸长率的变化率3 | 100°C,70hr,在ASTM#3油中 | ASTMD471 | -22 | % |
| 硬度计硬度的变化率3 | 支撐A,100°C,70hr,在ASTM#1油中 | ASTMD471 | -1.0 | |
| 硬度计硬度的变化率3 | 支撐A,100°C,70hr,在ASTM#3油中 | ASTMD471 | -12 | |
| 体积变化3 | 100°C,70hr,ASTM标准油（1号） | ASTMD471 | 2.0 | % |
| 体积变化3 | 100°C,70hr,ASTM标准油（3号） | ASTMD471 | 22 | % |
| 热损耗 | | ASTMD5688 | 0.20 | % |