| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | | 0.980 | g/cm3 |
| 门尼粘度(ML1+4,100°C) | | ASTMD1646 | 48 | MU |
| AcrylonitrileContent-Bound | | 内部方法 | 26.5 | % |
| Stabilizer | | | Non-staining | |
| 肖氏硬度2(邵氏A) | | ASTMD2240 | 80 | |
| Abrasion-Test,c.c3 | | DIN53516 | 53 | |
| 拉伸应力4(300%应变) | | ASTMD412 | 15.7 | MPa |
| 抗张强度2(屈服) | | ASTMD412 | 25.0 | MPa |
| 伸长率4(断裂) | | ASTMD412 | 460 | % |
| 撕裂强度5,2 | | ASTMD624 | 53.9 | kN/m |
| 压缩永久变形2(100°C,70hr) | | ASTMD395 | 57 | % |
| 空气中拉伸强度的变化率2(100°C,70hr) | | ASTMD865 | 7.0 | % |
| 空气中极限伸长率的变化率2(100°C,70hr) | | ASTMD865 | -26 | % |
| 空气中硬度计硬度的变化率2(邵氏A,100°C,70hr) | | ASTMD865 | 5.0 | |
| 拉伸强度的变化率2 | 100°C,70hr,在ASTM#1油中 | ASTMD471 | 9.0 | % |
| 拉伸强度的变化率2 | 100°C,70hr,在ASTM#3油中 | ASTMD471 | -14 | % |
| 极限伸长率的变化率2 | 100°C,70hr,在ASTM#1油中 | ASTMD471 | -28 | % |
| 极限伸长率的变化率2 | 100°C,70hr,在ASTM#3油中 | ASTMD471 | -20 | % |
| 硬度计硬度的变化率2 | 支撐A,100°C,70hr,在ASTM#1油中 | ASTMD471 | 7.0 | |
| 硬度计硬度的变化率2 | 支撐A,100°C,70hr,在ASTM#3油中 | ASTMD471 | -6.0 | |
| 体积变化2 | 100°C,70hr,ASTM标准油（1号） | ASTMD471 | -4.6 | % |
| 体积变化2 | 100°C,70hr,ASTM标准油（3号） | ASTMD471 | 14 | % |
| 热损耗 | | ASTMD5688 | 0.40 | % |
| AbrasionIndex-NBStest | | ASTMD1630 | 911 | |