| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | | 1.00 | g/cm3 |
| 门尼粘度 | ML1+4,100°C | ASTMD1646 | 51 | MU |
| 门尼粘度 | ML1+4,100°C2 | ASTMD1646 | 78 | MU |
| AcrylonitrileContent-Bound | | 内部方法 | 40.0 | % |
| Stabilizer | | | Non-staining | |
| 可溶性-inMEK | | | 100 | % |
| 肖氏硬度 | 邵氏A,5秒3 | ASTMD2240 | 76 | |
| 肖氏硬度 | 邵氏A,5秒4 | ASTMD2240 | 77 | |
| 肖氏硬度 | 邵氏A,5秒5 | ASTMD2240 | 78 | |
| 拉伸应力 | 300%应变3 | ASTMD412 | 10.9 | MPa |
| 拉伸应力 | 300%应变4 | ASTMD412 | 12.8 | MPa |
| 拉伸应力 | 300%应变5 | ASTMD412 | 13.3 | MPa |
| 抗张强度 | 屈服3 | ASTMD412 | 26.4 | MPa |
| 抗张强度 | 屈服4 | ASTMD412 | 26.8 | MPa |
| 抗张强度 | 屈服5 | ASTMD412 | 26.0 | MPa |
| 伸长率 | 断裂3 | ASTMD412 | 590 | % |
| 伸长率 | 断裂4 | ASTMD412 | 540 | % |
| 伸长率 | 断裂5 | ASTMD412 | 520 | % |
| 撕裂强度6,4 | | ASTMD624 | 58.0 | kN/m |
| 压缩永久变形5(100°C,70hr) | | ASTMD395 | 59 | % |
| 空气中拉伸强度的变化率7(100°C,70hr) | | ASTMD573 | -1.0 | % |
| 空气中极限伸长率的变化率7(100°C,70hr) | | ASTMD573 | -22 | % |
| 空气中硬度计硬度的变化率7(邵氏A,100°C,70hr) | | ASTMD573 | 5.0 | |
| 拉伸强度的变化率7 | 100°C,70hr,在ASTM#1油中 | ASTMD471 | -11 | % |
| 拉伸强度的变化率7 | 100°C,70hr,在IRM903油中 | ASTMD471 | -26 | % |
| 极限伸长率的变化率7 | 100°C,70hr,在ASTM#1油中 | ASTMD471 | -28 | % |
| 极限伸长率的变化率7 | 100°C,70hr,在IRM903油中 | ASTMD471 | -28 | % |
| 硬度计硬度的变化率7 | 支撐A,100°C,70hr,在ASTM#1油中 | ASTMD471 | 3.0 | |
| 硬度计硬度的变化率7 | 支撐A,100°C,70hr,在IRM903油中 | ASTMD471 | -5.0 | |
| 体积变化7 | 100°C,70hr,ASTM标准油（1号） | ASTMD471 | -0.20 | % |
| 体积变化7 | 100°C,70hr,在IRM903油中 | ASTMD471 | 8.5 | % |
| 热损耗 | | ASTMD5688 | 0.30 | % |