| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | | 0.970 | g/cm3 |
| 门尼粘度(ML1+4,100°C) | | ASTMD1646 | 46 | MU |
| AcrylonitrileContent-Bound | | 内部方法 | 28.0 | % |
| Stabilizer | | | Non-staining | |
| 可溶性-inMEK | | | 100 | % |
| 肖氏硬度 | 邵氏A2 | ASTMD2240 | 70 | |
| 肖氏硬度 | 邵氏A3 | ASTMD2240 | 71 | |
| 肖氏硬度 | 邵氏A4 | ASTMD2240 | 72 | |
| 拉伸应力 | 300%应变5 | ASTMD412 | 8.53 | MPa |
| 拉伸应力 | 300%应变6 | ASTMD412 | 9.02 | MPa |
| 拉伸应力 | 300%应变7 | ASTMD412 | 9.71 | MPa |
| 抗张强度 | 屈服2 | ASTMD412 | 27.6 | MPa |
| 抗张强度 | 屈服3 | ASTMD412 | 27.7 | MPa |
| 抗张强度 | 屈服4 | ASTMD412 | 27.3 | MPa |
| 伸长率 | 断裂5 | ASTMD412 | 680 | % |
| 伸长率 | 断裂6 | ASTMD412 | 640 | % |
| 伸长率 | 断裂7 | ASTMD412 | 610 | % |
| 撕裂强度8,3 | | ASTMD624 | 57.9 | kN/m |
| 压缩永久变形4(100°C,70hr) | | ASTMD395 | 55 | % |
| 空气中拉伸强度的变化率3(100°C,70hr) | | ASTMD865 | -9.0 | % |
| 空气中极限伸长率的变化率3(100°C,70hr) | | ASTMD865 | -30 | % |
| 空气中硬度计硬度的变化率3(邵氏A,100°C,70hr) | | ASTMD865 | 4.0 | |
| 拉伸强度的变化率3 | 100°C,70hr,在ASTM#1油中 | ASTMD471 | -15 | % |
| 拉伸强度的变化率3 | 100°C,70hr,在ASTM#3油中 | ASTMD471 | -34 | % |
| 极限伸长率的变化率3 | 100°C,70hr,在ASTM#1油中 | ASTMD471 | -25 | % |
| 极限伸长率的变化率3 | 100°C,70hr,在ASTM#3油中 | ASTMD471 | -30 | % |
| 硬度计硬度的变化率3 | 支撐A,100°C,70hr,在ASTM#1油中 | ASTMD471 | 0.0 | |
| 硬度计硬度的变化率3 | 支撐A,100°C,70hr,在ASTM#3油中 | ASTMD471 | -13 | |
| 体积变化3 | 100°C,70hr,ASTM标准油（1号） | ASTMD471 | 2.0 | % |
| 体积变化3 | 100°C,70hr,ASTM标准油（3号） | ASTMD471 | 23 | % |
| 热损耗 | | ASTMD5688 | 0.30 | % |