| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.75to1.80 | g/cm3 |
| 熔流率（熔体流动速率） | 230°C/2.16kg | ASTMD1238 | 5.5to11 | g/10min |
| 熔流率（熔体流动速率） | 230°C/5.0kg | ASTMD1238 | 16to30 | g/10min |
| 熔流率（熔体流动速率） | 收缩率-流动 | ASTMD1238 | 2.0to3.0 | % |
| 吸水率(23°C,24hr) | | ASTMD570 | <0.040 | % |
| 拉伸模量2(23°C,2.00mm) | | ASTMD638 | 1800to2500 | MPa |
| TensileStrength3(Yield,23°C,2.00mm) | | ASTMD638 | 50.0to60.0 | MPa |
| TensileStrength3(Break,23°C,2.00mm) | | ASTMD638 | 30.0to50.0 | MPa |
| TensileElongation3(Yield,23°C,2.00mm) | | ASTMD638 | 5.0to10 | % |
| TensileElongation3(Break,23°C,2.00mm) | | ASTMD638 | 20to300 | % |
| 摩擦系数 | 与自身-动态 | ASTMD1894 | 0.15to0.35 | |
| 摩擦系数 | 与自身-静态 | ASTMD1894 | 0.20to0.40 | |
| TaberAbrasionResistance(1000Cycles,1000g,CS-10Wheel) | | ASTMD4060 | 5.00to10.0 | mg |
| CharpyNotchedImpactStrength4(23°C,4.00mm) | | ASTMD6110 | 40.0to120 | J/m |
| DurometerHardness(ShoreD,1sec,2.00mm) | | ASTMD2240 | 73to80 | |
| 玻璃转化温度 | | ASTMD4065 | -40.0 | °C |
| 维卡软化温度 | | ASTMD15255 | 135to145 | °C |
| 熔融温度 | | ASTMD3418 | 170to175 | °C |
| 结晶峰温度(DSC)12 | | ASTMD3418 | 134to144 | °C |
| CLTE-Flow(0to40°C) | | ASTMD696 | 1.4E-4 | cm/cm/°C |
| 比热 | 23°C | ASTME968 | 1200 | J/kg/°C |
| 比热 | 100°C | ASTME968 | 1600 | J/kg/°C |
| 导热系数(23°C) | | ASTMC177 | 0.20 | W/m/K |
| 结晶热 | | ASTMD3417 | 54.0to60.0 | J/g |
| 融合热量 | | ASTMD3417 | 58.0to67.0 | J/g |
| 表面电阻率 | | ASTMD257 | >1.0E+14 | ohms |
| 体积电阻率 | | ASTMD257 | >1.0E+14 | ohmscm |
| 介电强度(23°C,1.00mm) | | ASTMD149 | 20to25 | kV/mm |
| 介电常数(23°C,1kHz) | | ASTMD150 | 7.00to10.0 | |
| UL阻燃等级(0.200mm) | | UL94 | V-0 | |
| 极限氧指数(3.00mm) | | ASTMD2863 | 44 | % |