性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.75to1.80 | g/cm3 |
熔流率(熔体流动速率)(230°C/5.0kg) | | ASTMD1238 | 3.0to9.0 | g/10min |
吸水率(23°C,24hr) | | ASTMD570 | <0.040 | % |
拉伸模量2(23°C,2.00mm) | | ASTMD638 | 360to480 | MPa |
TensileStrength3(Yield,23°C,2.00mm) | | ASTMD638 | 15.0to18.0 | MPa |
TensileStrength3(Break,23°C,2.00mm) | | ASTMD638 | 20.0to40.0 | MPa |
TensileElongation3(Yield,23°C,2.00mm) | | ASTMD638 | 12to15 | % |
TensileElongation3(Break,23°C,2.00mm) | | ASTMD638 | 600to750 | % |
玻璃转化温度 | | ASTMD4065 | -40.0 | °C |
熔融温度 | | ASTMD3418 | 130to136 | °C |
结晶峰温度(DSC)12 | | ASTMD3418 | 89.0to93.0 | °C |
结晶热 | | ASTMD3417 | 20.0to24.0 | J/g |
融合热量 | | ASTMD3417 | 20.0to24.0 | J/g |
表面电阻率 | | ASTMD257 | >1.0E+14 | ohms |
体积电阻率 | | ASTMD257 | >1.0E+14 | ohmscm |