性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 0.934 | g/cm3 |
表观密度2 | | ASTMD1895 | 0.34 | g/cm3 |
熔流率(熔体流动速率)(190°C/2.16kg) | | ASTMD1238 | 5.0 | g/10min |
EnvironmentalStress-CrackingResistance(100%Igepal,RotationalMolded,F50) | | ASTMD1693B | 1000 | hr |
TensileStrength(Yield,RotationalMolded) | | ASTMD638 | 19.3 | MPa |
TensileElongation(Break,RotationalMolded) | | ASTMD638 | 400 | % |
FlexuralModulus-Tangent(RotationalMolded) | | ASTMD790 | 793 | MPa |
ImpactStrength3(-40°C,RotationalMolded) | | ARM | 92 | J |
载荷下热变形温度(0.45MPa,未退火,滚塑成形) | | ASTMD648 | 63.0 | °C |
DeflectionTemperatureUnderLoad(1.8MPa,Unannealed,RotationalMolded) | | ASTMD648 | 42.0 | °C |
UL阻燃等级 | 1.5mm | UL94 | HB | |
UL阻燃等级 | 3.0mm | UL94 | HB | |
补充信息 | | TestMethod | NominalValue | Unit |
Pourability2 | | ASTMD1895 | 30.0 | sec |