| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.73 | g/cm3 |
| 密度 | | ASTMD792 | 1.73 | g/cm3 |
| 收缩率-流量(24小时) | | ASTMD955 | 0.40 | % |
| MoldingShrinkage-AcrossFlow(24hr) | | ASTMD955 | 1.0 | % |
| 吸水率(24hr,50%RH) | | ASTMD570 | 0.010 | % |
| 吸水率(平衡,23°C,50%RH) | | ISO62 | 0.010 | % |
| 拉伸模量2 | | ASTMD638 | 14200 | MPa |
| 拉伸模量 | | ISO527-2/1 | 11200 | MPa |
| 抗张强度3(屈服) | | ASTMD638 | 101 | MPa |
| 拉伸应力(屈服) | | ISO527-2/5 | 95.0 | MPa |
| 抗张强度3(断裂) | | ASTMD638 | 98.0 | MPa |
| 拉伸应力(断裂) | | ISO527-2/5 | 88.0 | MPa |
| 伸长率3(屈服) | | ASTMD638 | 5.6 | % |
| 拉伸应变(屈服) | | ISO527-2/5 | 5.0 | % |
| 伸长率4(断裂) | | ASTMD638 | 5.9 | % |
| 拉伸应变(断裂) | | ISO527-2/5 | 5.5 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 10600 | MPa |
| 弯曲模量5 | | ISO178 | 10400 | MPa |
| FlexuralStress5,6 | | ISO178 | 135 | MPa |
| 弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 143 | MPa |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 410 | J/m |
| NotchedIzodImpactStrength7(23°C) | | ISO180/1A | 34 | kJ/m2 |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD4812 | 480 | J/m |
| UnnotchedIzodImpactStrength7(23°C) | | ISO180/1U | 88 | kJ/m2 |
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | | ASTMD3763 | 20.0 | J |
| 多轴向仪器化冲击能量 | | ISO6603-2 | 8.00 | J |
| 载荷下热变形温度(0.45MPa,未退火,3.20mm) | | ASTMD648 | 248 | °C |
| HeatDeflectionTemperature8(0.45MPa,Unannealed,64.0mmSpan) | | ISO75-2/Bf | 239 | °C |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 214 | °C |
| HeatDeflectionTemperature8(1.8MPa,Unannealed,64.0mmSpan) | | ISO75-2/Af | 187 | °C |
| 线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 1.7E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 7.2E-5 | cm/cm/°C |