| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.04 | g/cm3 |
| 熔流率（熔体流动速率）(280°C/5.0kg) | | ASTMD1238 | 20 | g/10min |
| 溶化体积流率（MVR）(280°C/5.0kg) | | ISO1133 | 20.9 | cm3/10min |
| 拉伸模量 | | ISO527-2/1 | 1450 | MPa |
| 抗张强度2(屈服) | | ASTMD638 | 37.0 | MPa |
| 拉伸应力(屈服) | | ISO527-2/50 | 39.0 | MPa |
| 抗张强度2(断裂) | | ASTMD638 | 37.0 | MPa |
| 拉伸应力(断裂) | | ISO527-2/50 | 37.0 | MPa |
| 伸长率2(屈服) | | ASTMD638 | 37 | % |
| 拉伸应变(屈服) | | ISO527-2/50 | 17 | % |
| 伸长率2(断裂) | | ASTMD638 | 45 | % |
| 拉伸应变(断裂) | | ISO527-2/50 | 38 | % |
| 弯曲模量4(50.0mm跨距) | | ASTMD790 | 1150 | MPa |
| 弯曲模量4 | | ISO178 | 1260 | MPa |
| FlexuralStress4,5 | | ISO178 | 44.0 | MPa |
| 弯曲强度4(屈服,50.0mm跨距) | | ASTMD790 | 41.0 | MPa |
| CharpyNotchedImpactStrength6(23°C) | | ISO179/1eA | 43 | kJ/m2 |
| 悬壁梁缺口冲击强度(23°C) | | ASTMD256 | 550 | J/m |
| 悬壁梁缺口冲击强度7 | -30°C | ISO180/1A | 9.0 | kJ/m2 |
| 悬壁梁缺口冲击强度7 | 23°C | ISO180/1A | 41 | kJ/m2 |
| 装有测量仪表的落镖冲击 | -30°C,TotalEnergy | ASTMD3763 | 42.0 | J |
| 装有测量仪表的落镖冲击 | 23°C,TotalEnergy | ASTMD3763 | 33.0 | J |
| DurometerHardness(ShoreD,30sec) | | ASTMD2240 | 65 | |
| 载荷下热变形温度(0.45MPa,未退火,3.20mm) | | ASTMD648 | 115 | °C |
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | | ASTMD648 | 84.0 | °C |
| HeatDeflectionTemperature8(1.8MPa,Unannealed,64.0mmSpan) | | ISO75-2/Af | 93.0 | °C |
| 维卡软化温度 | | ASTMD15259 | 71.0 | °C |
| 维卡软化温度 | —— | ISO306/B50 | 71.0 | °C |
| 维卡软化温度 | —— | ISO306/B120 | 76.0 | °C |
| 线形热膨胀系数-流动(-40到40°C) | | ASTME831 | 8.2E-5 | cm/cm/°C |
| 线形热膨胀系数-横向(-40到40°C) | | ASTME831 | 1.3E-4 | cm/cm/°C |
| 相对电容率(1MHz) | | IEC60250 | 2.55 | |
| 耗散因数(1MHz) | | IEC60250 | 2.0E-3 | |