| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
| 比重 | | ASTMD792 | 1.04 | g/cm3 |
| 熔流率（熔体流动速率） | 210°C/5.0kg | ASTMD1238 | 15 | g/10min |
| 熔流率（熔体流动速率） | 250°C/2.16kg | ASTMD1238 | 17 | g/10min |
| 收缩率-流量(24小时) | | ASTMD955 | 0.55 | % |
| MoldingShrinkage-AcrossFlow(24hr) | | ASTMD955 | 0.65 | % |
| 吸水率2(23°C,24hr) | | ASTMD570 | 0.060 | % |
| 抗张强度3(断裂) | | ASTMD638 | 15.0 | MPa |
| 拉伸应力(断裂) | | ISO527-2/50 | 15.0 | MPa |
| 伸长率4(断裂) | | ASTMD638 | 150 | % |
| 拉伸应变(断裂) | | ISO527-2/50 | 140 | % |
| FlexuralModulus4(100mmSpan) | | ASTMD790 | 180 | MPa |
| 弯曲模量4 | | ISO178 | 200 | MPa |
| 肖氏硬度(邵氏A,30秒) | | ASTMD2240 | 88 | |
| 脆化温度 | | ASTMD746 | <-40.0 | °C |
| 体积电阻率 | | ASTMD257 | 7.1E+15 | ohmscm |
| ElectricStrength(2.00mm,inOil) | | IEC60243-1 | 25 | kV/mm |
| 相对电容率(1MHz) | | IEC60250 | 2.80 | |
| 耗散因数(1MHz) | | IEC60250 | 0.029 | |
| 漏电起痕指数 | | IEC60112 | 600 | V |
| UL阻燃等级(6.0mm) | | UL94 | V-0 | |
| 灼热丝易燃指数(3.0mm) | | IEC60695-2-12 | 850 | °C |
| 热灯丝点火温度(3.0mm) | | IEC60695-2-13 | 725 | °C |
| 极限氧指数 | | ISO4589-2 | 24 | % |