性能项目 | 试验条件[状态] | 测试方法 | 测试数据 |
比重 | | ASTMD792 | 1.33 | g/cm3 |
熔流率(熔体流动速率)(250°C/10.0kg) | | ASTMD1238 | 8.5 | g/10min |
抗张强度 | 断裂 | UL1581 | 15.0 | MPa |
抗张强度 | 断裂2 | ASTMD638 | 9.00 | MPa |
抗张强度 | Break,80°C3 | UL1581 | 15.0 | MPa |
拉伸应力(断裂) | | ISO527-2/50 | 9.00 | MPa |
伸长率 | 断裂 | UL1581 | 310 | % |
伸长率 | 断裂2 | ASTMD638 | 130 | % |
伸长率 | Break,80°C3 | UL1581 | 270 | % |
拉伸应变(断裂) | | ISO527-2/50 | 180 | % |
FlexuralModulus4(100mmSpan) | | ASTMD790 | 160 | MPa |
弯曲模量4 | | ISO178 | 135 | MPa |
肖氏硬度(邵氏A,30秒) | | ASTMD2240 | 93 | |
脆化温度 | | ASTMD746 | <-40.0 | °C |
HeatDeformation5(100°C) | | UL1581 | 10 | % |
体积电阻率 | | ASTMD257 | 2.0E+15 | ohmscm |
ElectricStrength(2.00mm,inOil) | | IEC60243-1 | 23 | kV/mm |
介电常数(1MHz) | | ASTMD150 | 3.00 | |
耗散因数(1MHz) | | ASTMD150 | 1.0E-3 | |
漏电起痕指数 | | IEC60112 | 600 | V |
灼热丝易燃指数(3.0mm) | | IEC60695-2-12 | 750 | °C |
热灯丝点火温度(3.0mm) | | IEC60695-2-13 | 775 | °C |
极限氧指数 | | ISO4589-2 | 29 | % |
烟雾密度 | Flame,0.5mmplaque,Ds,max | ASTME662 | 56 | |
烟雾密度 | Non-Flame,0.5mmplaque,Ds,max | ASTME662 | 150 | |
VerticalFlameTest | | EN50265-2-1 | PASSES | |